Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD | % | 1.0 | -- |
| Modeling Shrinkage | MD | % | 0.30 | -- |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | MPa | 10700 | 11300 |
| Tensile Stress | Break | MPa | 145 | |
| Tensile Strain | Break | % | 2.1 | 1.9 |
| Flexural Modulus | | MPa | 9800 | 10800 |
| Flexural Stress | | MPa | 225 | |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| RTIElec | 0.400mm | °C | 140 | -- |
| RTIElec | 0.750mm | °C | 140 | -- |
| RTIElec | 1.50mm | °C | 140 | -- |
| RTIElec | 3.00mm | °C | 140 | -- |
| Heat Deflection Temperature | 1.8MPa,Unannealed | °C | 281 | -- |
| Melting Temperature | | °C | 310 | -- |
| Coefficient of Linear Thermal Expansion | MD | cm/cm/°C | 1.8E-05 | -- |
| Coefficient of Linear Thermal Expansion | MD:-40to23°C | cm/cm/°C | 1.8E-05 | -- |
| Coefficient of Linear Thermal Expansion | MD:55to160°C | cm/cm/°C | 1.2E-05 | -- |
| Coefficient of Linear Thermal Expansion | TD | cm/cm/°C | 6.2E-05 | -- |
| Coefficient of Linear Thermal Expansion | TD:-40to23°C | cm/cm/°C | 6E-05 | -- |
| Coefficient of Linear Thermal Expansion | TD:55to160°C | cm/cm/°C | 9.5E-05 | -- |
| Electrical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Comparative Tracking Index | | V | 600 | -- |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | kJ/m² | 40 | |
| Charpy Unnotched Impact Strength | 23°C | kJ/m² | 45 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 0.400mm | | V-0 | -- |
| Flame Rating | 1.50mm | | V-0 | -- |
| Glow Wire Flammability Index | 0.400mm | °C | 960 | -- |
| Glow Wire Flammability Index | 3.00mm | °C | 960 | -- |
| Glow Wire Ignition Temperature | 0.400mm | °C | 700 | -- |
| Glow Wire Ignition Temperature | 3.00mm | °C | 775 | -- |
| Oxygen Index | | % | 37 | -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.