Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.14 | |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 1.2 | % |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Taber Abrasion Resistance | 1000g,CS-17 | ASTM D-1044 | 3.5%水|- | mg/1000次 |
Taber Abrasion Resistance | 1000g,CS-17 | ASTM D-1044 | 无水|8 | mg/1000次 |
Modeling Shrinkage | MD:1.00mm3 | % | 0.80到1.5 | -- |
Modeling Shrinkage | MD:3.00mm4 | % | 1.5到2.2 | -- |
Moisture Absorption | 23°C,24hr | % | 1.2 | -- |
Moisture Absorption | Saturation,23°C | % | 8.0 | -- |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength(Yield) | -40℃ | ASTM D-638 | 无水|1150 | kg/cm2 |
Tensile Strength(Yield) | -40℃ | ASTM D-638 | 3.5%水|1100 | kg/cm2 |
Flexural Stress | -40℃ | ASTM D-790 | 无水|1450 | kg/cm2 |
Tensile Stress | -40°C | MPa | 115 | |
Tensile Stress | 23°C | MPa | 80.0 | 50.0 |
Tensile Stress | 80°C | MPa | 40.0 | 40.0 |
Tensile Strain | Yield,23°C | % | 1.5 | -- |
Tensile Strain | Break,23°C | % | 25 | |
Flexural Modulus | -40°C | MPa | 4300 | 4100 |
Flexural Modulus | 23°C | MPa | 2900 | 1400 |
Flexural Modulus | 80°C | MPa | 900 | 500 |
Tensile Strength(Yield) | 23℃ | ASTM D-638 | 3.5%水|530 | kg/cm2 |
Compressive Strength | 23℃ | ASTM D-695 | 无水|910 | kg/cm2 |
Compressive Strength | 23℃ | ASTM D-695 | 3.5%水|- | kg/cm2 |
Flexural Stress | 23℃ | ASTM D-790 | 无水|1150 | kg/cm2 |
Flexural Stress | 23℃ | ASTM D-790 | 3.5%水|650 | kg/cm2 |
Tensile Strength(Yield) | 80℃ | ASTM D-638 | 无水|430 | kg/cm2 |
Tensile Strength(Yield) | 80℃ | ASTM D-638 | 3.5%水|400 | kg/cm2 |
Flexural Modulus | 23℃ | ASTM D-790 | 3.5%水|14000 | kg/cm2 |
Tensile Strength(Yield) | 23℃ | ASTM D-638 | 无水|800 | kg/cm2 |
Flexural Modulus | -40℃ | ASTM D-790 | 无水|44000 | kg/cm2 |
Flexural Modulus | -40℃ | ASTM D-790 | 3.5%水|42000 | kg/cm2 |
Rockwell Hardness | 23℃ | ASTM D-785 | 无水|97 | M-标度 |
Rockwell Hardness | 23℃ | ASTM D-785 | 3.5%水|- | M-标度 |
Tensile Strength | 23℃ | ASTM D-732 | 无水|790 | kg/cm2 |
Flexural Stress | -40℃ | ASTM D-790 | 3.5%水|1300 | kg/cm2 |
Tensile Elongation (Break) | 23℃ | ASTM D-638 | 无水|90 | % |
Tensile Elongation (Break) | 23℃ | ASTM D-638 | 3.5%水|< 200 | % |
Flexural Strength | | ASTM D790/ISO 178 | 2.8 | kg·cm/cm(J/M)ft·lb/in |
Tensile Strength | 23℃ | ASTM D-732 | 3.5%水|770 | kg/cm2 |
Flexural Stress | 80℃ | ASTM D-790 | 无水|640 | kg/cm2 |
Flexural Stress | 80℃ | ASTM D-790 | 3.5%水|400 | kg/cm2 |
Flexural Modulus | 80℃ | ASTM D-790 | 无水|9000 | kg/cm2 |
Flexural Modulus | 80℃ | ASTM D-790 | 3.5%水|5000 | kg/cm2 |
Rockwell Hardness | 23℃ | ASTM D-785 | 无水|119 | R-标度 |
Rockwell Hardness | 23℃ | ASTM D-785 | 3.5%水|100 | R-标度 |
Flexural Modulus | 23℃ | ASTM D-790 | 无水|29000 | kg/cm2 |
Flexural Stress | -40°C | MPa | 140 | |
Flexural Stress | 23°C | MPa | 115 | 65.0 |
Flexural Stress | 80°C | MPa | 65.0 | 40.0 |
Compressive Stress | 23°C | MPa | 90.0 | -- |
Shearing Strength | 23°C | MPa | 80.0 | 75.0 |
Taber Abrasion Resistance | 1000Cycles | mg | 8.00 | -- |
Coefficient of Friction (vs.Metal) | | | 0.15到0.20 | -- |
Izod Impact Strength | 23℃,Unnotched1/8 | | 3.5%水|- | kg·cm/cm2 |
Izod Impact Strength | 23℃,VNotched1/2 | ASTM D-256 | 无水|5 | kg·cm/cm |
Izod Impact Strength | 23℃,VNotched1/2 | ASTM D-256 | 3.5%水|28 | kg·cm/cm |
Izod Impact Strength | -40℃,VNotched1/2 | ASTM D-256 | 无水|3.5 | kg·cm/cm |
Izod Impact Strength | -40℃,VNotched1/2 | ASTM D-256 | 3.5%水|- | kg·cm/cm |
Izod Impact Strength | 23℃,Unnotched1/8 | | 无水|无断裂 | kg·cm/cm2 |
Charpy Impact Strength | | ASTM D256/ISO 179 | 50 | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Burning Rate | | UL94 | V-2 | |
Heat Deflection Temperature | | ASTM D648/ISO 75 | 220(0.46MPa) | ℃(℉) |
Coefficient of Linear Thermal Expansion | | ASTM D696/ISO 11359 | 0.32 | mm/mm.℃ |
Deflection Temperature Under Load | 4.6kg/cm2 | ASTM D-648 | 无水|220 | °C |
Deflection Temperature Under Load | 4.6kg/cm2 | ASTM D-648 | 3.5%水|- | °C |
Melting Temperature | | 差示扫描测热计DSC | 无水|265 | °C |
Melting Temperature | | 差示扫描测热计DSC | 3.5%水|- | °C |
Specific Heat | | | 无水|0.4 | Cal/g·℃ |
Specific Heat | | | 3.5%水|- | Cal/g·℃ |
Coefficient of Linear Thermal Expansion | | ASTM D-696 | 无水|9-10 | ×10-5cm/cm/℃ |
Coefficient of Linear Thermal Expansion | | ASTM D-696 | 3.5%水|- | ×10-5cm/cm/℃ |
Flame Rating | 1/32" | UL 94 | 无水|V-2 | |
Flame Rating | 1/32" | UL 94 | 3.5%水|- | |
Thermal Conductivity | | | 无水|0.21 | Kcal/m·hr·℃ |
Thermal Conductivity | | | 3.5%水|- | Kcal/m·hr·℃ |
Heat Deflection Temperature | 0.45MPa,Unannealed | °C | 220 | -- |
Melting Temperature | | °C | 265 | -- |
Coefficient of Linear Thermal Expansion | MD | cm/cm/°C | 9.0E-5到1.0E-4 | -- |
Specific Heat | | J/kg/°C | 2100 | -- |
Thermal Conductivity | | W/m/K | 0.32 | -- |
Electrical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Volume Resistivity | | ohms·cm | 1.0E+13到1.0E+14 | 1.0E+12到1.0E+13 |
Dielectric Constant | 23°C,50Hz | | 1.60 | -- |
Dissipation Factor | 23°C,50Hz | | 0.060 | -- |
Comparative Tracking Index | CTI | V | 530 | -- |
Comparative Tracking Index | | UL 746 | 无水|- | V |
Comparative Tracking Index | | UL 746 | 3.5%水|530 | V |
Dielectric Constant | 50Hz | ASTM D-150 | 无水|1.6 | |
Dielectric Constant | 50Hz | ASTM D-150 | 3.5%水|- | |
Volume Resistivity | | ASTM D-257 | 无水|1014-1015 | Ω.cm |
Volume Resistivity | | ASTM D-257 | 3.5%水|1012-1013 | Ω.cm |
Dissipation Factor | 50Hz | ASTM D-150 | 无水|0.06 | |
Dissipation Factor | 50Hz | ASTM D-150 | 3.5%水|- | |
Dielectric Constant | | ASTM D150/IEC 60250 | 3.3 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -40°C | | 无断裂 | -- |
Charpy Unnotched Impact Strength | 23°C | | 无断裂 | -- |
Hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Sale,23°C | | 119 | |
Rockwell Hardness | R-Sale,80°C | | 97 | -- |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 0.79mm | | V-2 | -- |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 23℃,24hr | ASTM D-570 | 无水|1.2 | % |
Moisture Absorption | 23℃,24hr | ASTM D-570 | 3.5%水|- | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.