Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | 23°C | ISO 1183 | 1.37 | g/cm³ |
| Modeling Shrinkage | Across Flow : 3.00 mm | 内部方法 | 0.60 到 0.90 | % |
| Modeling Shrinkage | 流量 : 3.00 mm | 内部方法 | 0.20 到 0.50 | % |
| Moisture Absorption | 24 hr, 23°C | ISO 62 | 0.60 | % |
| Moisture Absorption | Saturation, 23°C | ISO 62 | 5.5 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | -40°C | ISO 527-2 | 235 | Mpa |
| Tensile Stress | 23°C | ISO 527-2 | 190 | Mpa |
| Tensile Stress | 80°C | ISO 527-2 | 120 | Mpa |
| Tensile Strain | Break, -40°C | ISO 527-2 | 2.0 | % |
| Tensile Strain | Break, 23°C | ISO 527-2 | 2.5 | % |
| Tensile Strain | Break, 80°C | ISO 527-2 | 5.0 | % |
| Flexural Modulus | -40°C | ISO 178 | 11600 | Mpa |
| Flexural Modulus | 23°C | ISO 178 | 9500 | Mpa |
| Flexural Modulus | 80°C | ISO 178 | 5800 | Mpa |
| Flexural Stress | -40°C | ISO 178 | 325 | Mpa |
| Flexural Stress | 23°C | ISO 178 | 290 | Mpa |
| Flexural Stress | 80°C | ISO 178 | 190 | Mpa |
| Compressive Stress | -40°C | ISO 604 | 250 | Mpa |
| Compressive Stress | 23°C | ISO 604 | 180 | Mpa |
| Compressive Stress | 80°C | ISO 604 | 110 | Mpa |
| Shearing Strength | 23°C | ASTM D732 | 95.0 | Mpa |
| Taber Abrasion Resistance | 1000 Cycles | ISO 9352 | 0.400 | mg |
| Coefficient of Friction (vs.Metal) | | Suzuki Method | 0.15 | |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 262 | °C |
| Melting Temperature | | DSC | 265 | °C |
| Coefficient of Linear Thermal Expansion (Flow) | | ISO 11359-2 | 2.0E-5 到 3.0E-5 | cm/cm/°C |
| Specific Heat | | | 1800 | J/kg/°C |
| Thermal Conductivity | | | 0.40 | W/m/K |
| Electrical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume Resistivity | | IEC 60093 | 1.0E+13 | ohms·cm |
| Dielectric Strength | | IEC 60243-1 | 20 | KV/mm |
| Dielectric Constant | 23°C, 50 Hz | IEC 60250 | 4.60 | |
| Dielectric Constant | 23°C, 1 kHz | IEC 60250 | 4.40 | |
| Dielectric Constant | 23°C, 1 MHz | IEC 60250 | 3.90 | |
| Dissipation Factor | 23°C, 50 Hz | IEC 60250 | 0.020 | |
| Dissipation Factor | 23°C, 1 kHz | IEC 60250 | 0.020 | |
| Dissipation Factor | 23°C, 1 MHz | IEC 60250 | 0.020 | |
| Arc Resistance | | UL 746 | 114 | sec |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -40°C | ISO 179 | 10 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 13 | kJ/m² |
| Charpy Unnotched Impact Strength | -40°C | ISO 179 | 60 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO 179 | 65 | kJ/m² |
| Hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | M -Sale, 23°C | ISO 2039-2 | 97 | |
| Rockwell Hardness | R -Sale, 80°C | ISO 2039-2 | 24 | |
| Rockwell Hardness | R -Sale, 23°C | ISO 2039-2 | 121 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 0.79 mm | UL 94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.