Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 24 | g/10min |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Volume flow Rate | 220°C/10.0kg | ISO1133 | 24.0 | cm3/10min |
Modeling Shrinkage | MD:23°C | ISO294-4 | 0.40到0.60 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | 23°C | ISO527-2 | 2200 | Mpa |
Tensile Stress | 23°C | ISO527-2 | 41.0 | Mpa |
Flexural Modulus | 23°C | ISO178 | 2300 | Mpa |
Flexural Stress | 23°C | ISO178 | 65.0 | Mpa |
Flexural Modulus | | ASTM D790/ISO 178 | 2,400 | kg/cm²(MPa)[Lb/in²] |
Charpy impact strength | | | 31 | kJ/m² |
Flexural Modulus | | | 2400 | Mpa |
Charpy Impact Strength | | ASTM D256/ISO 179 | 31 | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Heat Deflection Temperature | | | 80 | °C |
Heat Deflection Temperature | | ASTM D648/ISO 75 | 80 | ℃(℉) |
Heat Deflection Temperature | 1.8MPa,Unannealed | ISO75-2/Af | 80.0 | °C |
Coefficient of Linear Thermal Expansion | MD | ISO11359-2 | 8.5E-05 | cm/cm/°C |
Hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Sale,23°C | ISO2039-2 | 107 | |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | | | 24 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.