Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density / Specific Gravity | | ASTMD792 | 1.16 | g/cm³ |
Density / Specific Gravity | | ISO1183 | 1.16 | g/cm³ |
Melt Volume flow Rate | 275°C/5.0kg | ISO1133 | 140 | cm3/10min |
Modeling Shrinkage | MD:3.18mm | | 0.80 | % |
Moisture Absorption | Saturation | ASTMD570 | 8.5 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 8.5 | % |
Moisture Absorption | Equilibrium,50%RH | ASTMD570 | 2.9 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 2.9 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | 23°C | ISO527-2 | 3500 | Mpa |
Tensile Strength | Yield,23°C | ASTMD638 | 83.0 | Mpa |
Tensile Stress | Yield,23°C | ISO527-2 | 75.0 | Mpa |
Tensile Elongation | Yield,23°C | ASTMD638 | 5.0 | % |
Tensile Strain | Yield,23°C | ISO527-2 | 4.0 | % |
Tensile Elongation | Break,23°C | ASTMD638 | 50 | % |
Nominal Tensile Strain at Break | 23°C | ISO527-2 | 6.0 | % |
Flexural Modulus | 23°C | ASTMD790 | 3000 | Mpa |
Flexural Modulus | 23°C | ISO178 | 3000 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Coefficient of Linear Thermal Expansion | MD | | 8E-05 | cm/cm/°C |
Coefficient of Linear Thermal Expansion | TD | | 9E-05 | cm/cm/°C |
RTIElec | 0.38mm | UL746 | 110 | °C |
RTIElec | 0.75mm | UL746 | 120 | °C |
RTIElec | 1.5mm | UL746 | 120 | °C |
RTIElec | 3.0mm | UL746 | 120 | °C |
RTIImp | 0.38mm | UL746 | 65.0 | °C |
RTIImp | 0.75mm | UL746 | 105 | °C |
RTIImp | 1.5mm | UL746 | 105 | °C |
RTIImp | 3.0mm | UL746 | 105 | °C |
Heat Deflection Temperature | 0.45MPa,Unannealed | ASTMD648 | 224 | °C |
Heat Deflection Temperature | 1.8MPa,Unannealed | ASTMD648 | 91.0 | °C |
Heat Deflection Temperature | 1.8MPa,Unannealed | ISO75-2/A | 70.0 | °C |
Peak Melting Temperature | | ASTMD3418 | 243 | °C |
Melting Temperature | | ISO3146 | 243 | °C |
Coefficient of Linear Thermal Expansion | MD | ASTME831 | 4E-05 | cm/cm/°C |
RTIStr | 0.38mm | UL746 | 65.0 | °C |
RTIStr | 0.75mm | UL746 | 115 | °C |
RTIStr | 1.5mm | UL746 | 120 | °C |
RTIStr | 3.0mm | UL746 | 120 | °C |
Electrical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Volume Resistivity | 1.50mm | ASTMD257 | 1E+13 | ohms·cm |
Volume Resistivity | | IEC60093 | 1E+13 | ohms·cm |
Dielectric Strength | | IEC60243-1 | 32 | KV/mm |
Dielectric Constant | 1MHz | IEC60250 | 3.60 | |
Dissipation Factor | 1MHz | IEC60250 | 0.020 | |
Comparative Tracking Index | | IEC60112 | 600 | V |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod Impact Strength | -40°C | ASTMD256 | 32 | J/m |
Notched Izod Impact Strength | 23°C | ASTMD256 | 43 | J/m |
Notched Izod Impact Strength | 23°C | ISO180 | 4.5 | kJ/m² |
Charpy Notched Impact Strength | -30°C | ISO179 | 4.0 | kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO179 | 9.0 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179 | 80 | kJ/m² |
Hardness | Test Condition | Test Method | Test Result | Unit |
---|
Ball Indentation Hardness | | ISO2039-1 | 100 | Mpa |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 0.38mm | UL94 | V-0 | |
Flame Rating | 0.75mm | UL94 | V-0 | |
Flame Rating | 1.5mm | UL94 | V-0 | |
Flame Rating | 3.0mm | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.