ASA/PC GELOY™ HRA222F WH5D169 SABIC INNOVATIVE SAUDI
34
- Unit Price:
- $3702 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 62MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Melt Volume flow Rate | 260°C/2.16 kg | ISO 1133 | 13.0 | cm3/10min |
Modeling Shrinkage - Flow | 内部方法 | 0.40 到 0.60 | % | |
Moisture Absorption | Saturation, 23°C | ISO 62 | 0.60 | % |
Equilibrium, 23°C, 50% RH | ISO 62 | 0.20 | % | |
Outdoor Suitability | UL 746C | f1 |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Tensile Modulus | -- 3 | ASTM D638 | 2590 | Mpa |
-- | ISO 527-2/1 | 2520 | Mpa | |
Tensile Strength | Yield 4 | ASTM D638 | 63.0 | Mpa |
Yield 5 | ASTM D638 | 59.0 | Mpa | |
Yield | ISO 527-2/5 | 62.0 | Mpa | |
Yield | ISO 527-2/50 | 60.0 | Mpa | |
Break 5 | ASTM D638 | 66.0 | Mpa | |
Break 4 | ASTM D638 | 56.0 | Mpa | |
Break | ISO 527-2/5 | 51.0 | Mpa | |
Break | ISO 527-2/50 | 45.0 | Mpa | |
Tensile Elongation | Yield 5 | ASTM D638 | 4.2 | % |
Yield 4 | ASTM D638 | 4.3 | % | |
Yield | ISO 527-2/5 | 4.3 | % | |
Yield | ISO 527-2/50 | 4.4 | % | |
Break 5 | ASTM D638 | > 100 | % | |
Break 4 | ASTM D638 | > 100 | % | |
Break | ISO 527-2/5, ISO 527-2/50 | > 50 | % | |
Flexural Modulus | ISO 178 | 2510 | Mpa | |
Flexural Stress | ISO 178 | 93.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Heat Deflection Temperature | 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Be | 99.0 | °C |
1.8 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Ae | 88.0 | °C | |
Vicat Softening Temperature | -- | ISO 306/A50 | 111 | °C |
-- | ISO 306/B50 | 102 | °C | |
-- | ISO 306/B120 | 104 | °C | |
Ball PressureTest | 73 to 77°C | IEC 60695-10-2 | 通过 | |
Coefficient of Linear Thermal Expansion | Flow : -30 to 80°C | ISO 11359-2 | 6.9E-5 | cm/cm/°C |
Across Flow : -30 to 80°C | ISO 11359-2 | 7.1E-5 | cm/cm/°C | |
Across Flow : 23 to 80°C | ISO 11359-2 | 7.5E-5 | cm/cm/°C | |
RTI Elec | UL 746 | 90.0 | °C | |
RTI Imp | UL 746 | 90.0 | °C | |
RTI | UL 746 | 90.0 | °C |
Electrical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Comparative Tracking Index | UL 746 | PLC 0 | ||
Comparative Tracking Index | IEC 60112 | 600 | V |
Injection | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Drying Temperature | 80 到 90 | °C | ||
Drying Time | 2.0 到 4.0 | hr | ||
Suggested Max Moisture | 0.020 | % | ||
Hopper Temperature | 60 到 80 | °C | ||
Rear Temperature | 200 到 230 | °C | ||
Middle Temperature | 220 到 260 | °C | ||
Front Temperature | 230 到 270 | °C | ||
Nozzle Temperature | 220 到 260 | °C | ||
Processing (Melt) Temp | 230 到 270 | °C | ||
Mold Temperature | 50 到 70 | °C |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Flame Rating | 2.0 mm | UL 94 | V-0 | |
Oxygen Index | ISO 4589-2 | 29 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.