PC/PBT XENOY™ ENH2900-BK1066 SABIC INNOVATIVE US

Unit Price:
$3201 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
61MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate	266°C/5.0 kg	ASTM D1238	26	g/10 min
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.50 到 0.80	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Modulus		ASTM D638	2480	Mpa
Tensile Strength	Yield	ASTM D638	63.0	Mpa
Tensile Strength	Tensile Strength	Break	ASTM D638	42.0	Mpa
Tensile Elongation	Yield	ASTM D638	4.0	%
Tensile Elongation	Tensile Elongation	Break	ASTM D638	65	%
Flexural Modulus	50.0 mm Span	ASTM D790	2240	Mpa
Flexural Strength	Yield, 50.0 mm Span	ASTM D790	89.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	78.0	°C
Vicat Softening Temperature		ASTM D15255	102	°C

Injection	Test Result	Unit
Drying Temperature	80 到 90	°C
Drying Time	3.0 到 4.0	hr
Suggested Max Moisture	0.040	%
Suggested Shot Size	30 到 80	%
Rear Temperature	220 到 255	°C
Middle Temperature	220 到 265	°C
Front Temperature	245 到 275	°C
Nozzle Temperature	245 到 275	°C
Processing (Melt) Temp	245 到 275	°C
Mold Temperature	60 到 80	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.038 到 0.076	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	65.0	J

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	1.1 mm	UL 94	V-1
	Flame Rating	1.5 mm	UL 94	V-0
	Flame Rating	Flame Rating	2.5 mm	UL 94	5VB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.