Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 210°C/21.6kg | ASTMD1238 | 30到50 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod Impact Strength | -30°C | DIN 53453 | 不破裂 | kJ/m² |
Compression Set | | DIN 53517 | 25 | % |
Compression Set | 70°C | DIN 53517 | 40 | % |
Shore Hardness | | DIN 53505 | 41 | shoreB |
Tensile Modulus | 300% | DIN 53504-S2 | 15 | n/mm² |
Notched Izod Impact Strength | +23°C | DIN 53453 | 不破裂 | kJ/m² |
Tensile Modulus | 20% | DIN 53504-S2 | 7 | n/mm² |
Tensile Strength | 80℃水中21天 | DIN 53504-S2 | 40 | n/mm² |
Tensile Elongation (Break) | | DIN 53504-S2 | 550 | % |
Tearing Strength | | DIN 53515 | 95 | N/mm |
Taber Abrasion Resistance | | DIN 53516 | 25 | mm³ |
Tensile Strength | | DIN 53504-S2 | 55 | n/mm² |
Shore Hardness | | DIN 53505 | 93 | shoreA |
Tensile Elongation (Break) | 80℃水中21天 | DIN 53504-S2 | 550 | % |
Tensile Modulus | 100% | DIN 53504-S2 | 9 | n/mm² |
100% Secant | | ASTM D412/ISO 527 | 9 | Mpa/Psi |
300% Secant | | ASTM D412/ISO 527 | 15 | Mpa/Psi |
Tensile Strength | | ASTM D412/ISO 527 | 55 | Mpa/Psi |
Tearing Strength | | ASTM D624/ISO 34 | 95 | n/mm² |
Shore Hardness (Shore A) | | ASTM D2240/ISO 868 | 93 | Shore A |
Shore Hardness (Shore D) | | ASTM D2240/ISO 868 | 41 | Shore D |
Tensile Modulus | Injection | ASTMD412 | 39.3 | Mpa |
Flexural Modulus | Injection | ASTMD790 | 48.3 | Mpa |
Taber Abrasion Resistance | | ASTMD1044 | 25.0 | mg |
Abrasion-DIN | | DIN53516 | 25 | mm³ |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
SofteningPoint-DMA | | 内部方法 | 113 | °C |
Glass Transition Temperature | | 内部方法 | -38.0 | °C |
Vicat Softening Temperature | | ASTMD1525 | 128 | °C |
Elastomers Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | 100%Strain | ASTMD412 | 10.3 | Mpa |
Tensile Stress | 300%Strain | ASTMD412 | 22.8 | Mpa |
Tensile Strength | | ASTMD412 | 44.1 | Mpa |
Tensile Elongation | Break | ASTMD412 | 520 | % |
Tearing Strength | | ASTMD624 | 133 | kN/m |
Compression Set | 23°C,22hr | ASTMD395B | 25 | % |
Compression Set | 70°C,22hr | ASTMD395B | 40 | % |
Hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore A | ASTMD2240 | 90 | |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Density | | DIN 53479 | 1.20 | g/cm³ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.