Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density / Specific Gravity | | ISO1183 | 1.07 | g/cm³ |
Melt Volume flow Rate | 220°C/10.0kg | ISO1133 | 15.0 | cm3/10min |
Modeling Shrinkage | | ISO294-4 | 0.50to0.90 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 1.7 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.35 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ISO527-2 | 2300 | Mpa |
Tensile Stress | Yield,23°C | ISO527-2 | 48.0 | Mpa |
Tensile Strain | Yield,23°C | ISO527-2 | 3.3 | % |
Tensile Creep Modulus | 1hr | ISO899-1 | 1850 | Mpa |
Tensile Creep Modulus | 1000hr | ISO899-1 | 1400 | Mpa |
Flexural Stress | | ISO178 | 70.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Heat Deflection Temperature | 0.45MPa,Annealed | ISO75-2/B | 101 | °C |
Heat Deflection Temperature | 1.8MPa,Annealed | ISO75-2/A | 97.0 | °C |
Vicat Softening Temperature | -- | ISO306/A50 | 105 | °C |
Vicat Softening Temperature | -- | ISO306/B50 | 97.0 | °C |
Coefficient of Linear Thermal Expansion | MD | ISO11359-2 | 8.0E-5to1.1E-4 | cm/cm/°C |
Thermal Conductivity | | DIN52612 | 0.17 | W/m/K |
Electrical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | 1E+13 | ohms |
Volume Resistivity | | IEC60093 | 1E+14 | ohms·cm |
Dielectric Constant | 100Hz | IEC60250 | 3.70 | |
Dissipation Factor | 100Hz | IEC60250 | 0.011 | |
Dissipation Factor | 1MHz | IEC60250 | 0.024 | |
Films Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Elongation(MD) | Break | ISO527-3 | 9.0 | % |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | -30°C | ISO179 | 4.0 | kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO179 | 17 | kJ/m² |
Notched Izod Impact Strength | -30°C | ISO180/A | 4.0 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO180/A | 14 | kJ/m² |
Hardness | Test Condition | Test Method | Test Result | Unit |
---|
Ball Indentation Hardness | | ISO2039-1 | 80.0 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.