Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Volume flow Rate | 200℃，5 kg | | 5.8 | cm3/10min |
| Moisture Absorption | Saturation，23℃ | ISO 62 | 0.1 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Scale | ISO 2039-2 | 70 | |
| Tensile Modulus | 1 mm/min | ISO 527-2 | 2120 | Mpa |
| Tensile Strength | Yield，23℃ | ISO 527-2 | 39 | Mpa |
| Tensile Strain | Break，23℃ | ISO 527-2 | 36 | % |
| Flexural Modulus | -- | ISO 178 | 1890 | Mpa |
| Flexural Strength | -- | ISO 178 | 57 | Mpa |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | 23℃ | ISO 179 | 3.4 | kJ/m² |
| Gardner Impact | | ASTM D5420 | 11 | J |
| Optical | Test Condition | Test Method | Test Result | Unit |
|---|
| Transmittance | 3.2 mm | ASTM D1003 | 89 | % |
| Haze | | ISO 14782 | 1.5 | % |
| Thermal | Test Condition | Test Method | Test Result | Unit |
|---|
| Coefficient of Linear Thermal Expansion | | ISO 11359 | 0.8-1.1 | ×10-4/℃ |
| Thermal Conductivity | | DIN 5261-1 | 0.17 | W/m/K |
| Heat Deflection Temperature | 0.45 MPa，Annealed | ISO 75-2/B | 101 | °C |
| Heat Deflection Temperature | 1.8 MPa，Annealed | ISO 75-2/A | 87 | °C |
| Vicat Softening Temperature | B50 | ISO 306 | 74 | °C |
| Maximum Service Temperature | | | 250 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.