Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.57 | |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.03 | % |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
glass fiber content | | | 30 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | | ASTM D638 | 1240 | kg/cm |
Tensile Elongation | | ASTM D638 | 3.5 | % |
Impact Strength | | ASTM D256 | 8.7 | kg.cm/cm |
Tensile Modulus | | ASTM D790 | 85000 | kg/cm |
Flexural Stress | | ASTM D790 | 1750 | kg/cm |
Hardness | | ASTM D785 | 121 | R |
Tensile Strength | | ASTM D638/ISO 527 | 1240 | kg/cm²(MPa)[Lb/in²] |
Tensile Elongation | | ASTM D638/ISO 527 | 3.5 | % |
Rockwell Hardness | | ASTM D785 | 121 | |
Flexural Modulus | | ASTM D790/ISO 178 | 85000 | kg/cm²(MPa)[Lb/in²] |
Flexural Strength | | ASTM D790/ISO 178 | 1750 | kg/cm²(MPa)[Lb/in²] |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Burning Rate | | UL94 | V0 | |
Melting Temperature | | | 225 | ℃(℉) |
Coefficient of Linear Thermal Expansion | | ASTM D696/ISO 11359 | 3 | mm/mm.℃ |
Heat Deflection Temperature | 18.6kg/cm | ASTM D648 | 200(218) | °C |
Flame Rating | | UL94 | V-0 | |
Melting Temperature | | DSC | 225 | °C |
Coefficient of Linear Thermal Expansion | | ASTM D696 | 3 | |
Electrical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | ASTM D257 | 10 | Ω |
Volume Resistivity | | ASTM D257 | 10 | Ω.cm |
Dielectric Constant | 60Hz | ASTM D150 | 3.5 | |
Arc Resistance | | ASTM D495 | 90 | sec |
Dielectric Constant | 60Hz | ASTM D150 | 0.001 | |
Insulation Resistance | | ASTM D149 | 22 | KV/mm |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | | ASTM D570 | 0.03 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.