PC Makrolon® RX2430 451118 COVESTRO THAILAND

384

Unit Price:US$ 5,317 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
57.8MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜High mobility
Application Areas:Automotive Applications｜Lighting installation｜electrical equipment
Color:--
Grade:Medical grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C, Complete Break	ISO 179/1eA	14 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C, Partial Break	ISO 179/1eA	70 kJ/m²
Impact strength of simply supported beam without notch	-60°C	ISO 179/1eU	无断裂
	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	-30°C, Complete Break	ISO 180/A	12 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C, Partial Break	ISO 180/A	60 kJ/m²
Multi axis Instrumented Impact Energy	-30°C	ISO 6603-2	70.0 J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	60.0 J
Multi axis Instrumented Peak Impact Force	-30°C	ISO 6603-2	6200 N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	5300 N

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.36 mm	UL 94	V-2
flash temperature		ASTM D1929	480 °C
auto-ignition temperature		ASTM D1929	550 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ISO 527-2/1	2400 Mpa
tensile strength	Yield, 23°C	ISO 527-2/50	67.0 Mpa
tensile strength	tensile strength	Break, 23°C	ISO 527-2/50	75.0 Mpa
Tensile strain	Yield, 23°C	ISO 527-2/50	6.1 %
Tensile strain	Tensile strain	Break, 23°C	ISO 527-2/50	130 %
Nominal tensile fracture strain	23°C	ISO 527-2/50	> 50 %
Bending modulus	23°C	ISO 178	2400 Mpa
bending strength	23°C	ISO 178	100 Mpa
	bending strength	3.5% Strain, 23°C	ISO 178	74.0 Mpa
	bending strength	bending strength	23°C	ISO 178	7.0 %

injection	Test Condition	Test Method	Test Result
Drying Temperature - Dry Air Dryer			120 °C
Drying time - Dry Air Dryer			4.0 hr
Suggested maximum moisture content			< 0.020 %
Suggested injection volume			30 to 70 %
Temperature at the rear of the barrel			250 to 270 °C
Temperature in the middle of the barrel			270 to 290 °C
Temperature at the front of the material cylinder			285 to 305 °C
Spray nozzle temperature			270 to 305 °C
Processing (melt) temperature			280 to 320 °C
Mold temperature			70 to 110 °C
Back pressure			10.0 to 20.0 Mpa
Exhaust hole depth			0.025 to 0.075 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	134 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	122 °C
Vicat softening temperature	--	ISO 306/B50	141 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	142 °C
Ball Pressure Test	132°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : 23 to 55°C	ISO 11359-2	6.5E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 55°C	ISO 11359-2	6.5E-5 cm/cm/°C
thermal conductivity	23°C	ISO 8302	0.20 W/m/K

Physical properties	Test Condition	Test Method	Test Result
Apparent density		ISO 60	0.66 g/cm³
melt mass-flow rate	300°C/1.2 kg	ISO 1133	20 g/10 min
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	19.0 cm3/10min
Shrinkage rate	横向Flow	ISO 2577	0.60 - 0.80 %
	Shrinkage rate	Flow	ISO 2577	0.60 - 0.80 %
		Shrinkage rate	横向Flow : 280°C, 2.00 mm3	ISO 294-4	0.65 %
		Shrinkage rate	Shrinkage rate	Flow : 2.00 mm3	ISO 294-4	0.60 %
Water absorption rate	Saturation, 23°C	ISO 62	0.30 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.12 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1.0E+16 ohms
Volume resistivity	23°C	IEC 60093	1.0E+16 ohms·cm

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test		ISO 2039-1	118 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.