PC/ABS INFINO® NH-1018 Samsung Cheil South Korea

249

Unit Price:US$ 4,282 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant
Application Areas:Tool handle｜TV
Color:--
Grade:Flame retardant grade

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	V-1
	UL flame retardant rating	2.0 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--3	ASTM D638	2000 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/50	45.0 Mpa
tensile strength	Yield3	ASTM D638	62.0 Mpa
	tensile strength	Yield	ISO 527-2/50	60.0 Mpa
	tensile strength	tensile strength	Break3	ASTM D638	51.0 Mpa
elongation	Break3	ASTM D638	15 %
elongation	elongation	Break	ISO 527-2/50	15 %
Bending modulus	--4	ASTM D790	2500 Mpa
Bending modulus	Bending modulus	--5	ISO 178	2700 Mpa
bending strength	--4	ASTM D790	83.0 Mpa
bending strength	bending strength	--5	ISO 178	90.0 Mpa

injection	Test Condition	Test Method	Test Result
Hot air dryer			80 °C
Vacuum drying machine			80 °C
Hot air dryer			4.0 hr
Vacuum drying machine			4.0 hr
Suggested maximum moisture content			0.050 %
Temperature at the rear of the barrel			230 to 240 °C
Temperature in the middle of the barrel			240 to 250 °C
Temperature at the front of the material cylinder			250 to 260 °C
Spray nozzle temperature			250 °C
Mold temperature			40 to 80 °C
Injection pressure			49.0 to 147 Mpa
Back pressure			0.490 to 1.96 Mpa
Screw speed			50 to 150 rpm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm	ISO 75-2/B	83.0 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	83.0 °C
Vicat softening temperature		ISO 306/B50	98.0 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	220°C/10.0 kg	ASTM D1238	35 g/10 min
Shrinkage rate	Flow : 3.20 mm	ASTM D955	0.40 - 0.70 %
	Shrinkage rate	Across FlowFlow : 3.20 mm	ASTM D955	0.40 - 0.70 %
		Shrinkage rate	横向Flow : 2.00 mm	ISO 294-4	0.40 - 0.70 %
		Shrinkage rate	Shrinkage rate	Flow : 2.00 mm	ISO 294-4	0.40 - 0.70 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	110
Rockwell hardness	Rockwell hardness	R -Sale	ISO 2039-2	110

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.