PC/ABS

PC/ABS INFINO® HM-1100 K21294 Samsung Cheil South Korea

237

Unit Price:US$ 4,028 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
24MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜Flame retardant｜Filler: Glass fiber reinforced material
Application Areas:Electronic and Electrical Applications｜TV
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.0 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	7.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	2.0mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	3400 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/5	3400 Mpa
tensile strength	Yield	ASTM D638	59.0 Mpa
	tensile strength	Yield	ISO 527-2/5	55.0 Mpa
		tensile strength	Break	ASTM D638	59.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/5	55.0 Mpa
elongation	Break	ASTM D638	4.0 %
Tensile strain	Break	ISO 527-2/5	4.0 %
Bending modulus		ASTM D790	3900 Mpa
Bending modulus	Bending modulus		ISO 178	3800 Mpa
bending strength		ASTM D790	96.0 Mpa
bending strength	bending strength		ISO 178	95.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	97.0 °C
	Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	97.0 °C
		Hot deformation temperature	0.45MPa,Annealed,4.00mm	ISO 75-2/B	102 °C
			Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	96.0 °C
				Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	96.0 °C
				Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed,4.00mm	ISO 75-2/A	98.0 °C
Vicat softening temperature		ISO 306/B50	99.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD	ASTM D955	0.10 %
	Shrinkage rate	TD	ISO 2577	0.10 %
	Shrinkage rate	Shrinkage rate	MD:3.20mm	ISO 2577	0.10 %
ash content	--	ISO 3451	9.5 %
	ash content	--	ASTM D5630	9.5 %
	ash content	ash content	Tg(halfwidth)-DSC		101 °C
melt mass-flow rate	220°C/10.0kg	ASTM D1238	22 g/10min
	melt mass-flow rate	250°C/2.16kg	ASTM D1238	7.0 g/10min
		melt mass-flow rate	220°C/10.0kg	ISO 1133	22 g/10min
		melt mass-flow rate	melt mass-flow rate	250°C/2.16kg	ISO 1133	7.0 g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	0.10 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	118
Rockwell hardness	Rockwell hardness	R-Scale	ISO 2039-2	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/ABS INFINO® HM-1100 K21294 Samsung Cheil South Korea

Material Description

Technical Data Sheet Compare

Technical Data Sheet