ABS

ABS STAREX® VH0815M NP Samsung Cheil South Korea

Unit Price:US$ 3,171 /MT
Packaging Specification:
Supply Quantity:
10MT
Delivery Terms:
DDP
:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Easy to process｜Flame retardant
Application Areas:Home appliance components｜Electrical enclosure
Color:--
Grade:Flame retardant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	20 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	19 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8mm	UL 94	V-2
	UL flame retardant rating	1.5mm	UL 94	V-1
		UL flame retardant rating	2.0mm	UL 94	V-0
			UL flame retardant rating	3.0mm	UL 94	V-0
			UL flame retardant rating	UL flame retardant rating	2.5mm	UL 94	5VA

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ASTM D638	40.5 Mpa
	tensile strength	Yield	ISO 527-2/50	46.0 Mpa
		tensile strength	Break	ASTM D638	31.5 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	34.0 Mpa
elongation	Break	ASTM D638	15 %
Tensile strain	Break	ISO 527-2/50	3.0 %
Bending modulus		ASTM D790	2180 Mpa
Bending modulus	Bending modulus		ISO 178	3480 Mpa
bending strength		ASTM D790	60.3 Mpa
bending strength	bending strength		ISO 178	73.0 Mpa
Tensile modulus		ASTM D638	2060 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/50	2270 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	85.0 °C
	Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	86.0 °C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	78.0 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	70.4 °C
Vicat softening temperature		ISO 306/B50	85.785.5 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	200°C/5.0kg	ASTM D1238	4.0 g/10min
melt mass-flow rate	melt mass-flow rate	200°C/5.0kg	ISO 1133	4.0 g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	0.31-0.59 %
	Shrinkage rate	TD：3.20mm	ASTM D955	0.31-0.59 %
		Shrinkage rate	TD:3.20mm	ISO 2577	0.31-0.59 %
		Shrinkage rate	Shrinkage rate	MD:3.20mm	ISO 2577	0.31-0.59 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	105
Rockwell hardness	Rockwell hardness	R-Scale	ISO 2039-2	103

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS STAREX® VH0815M NP Samsung Cheil South Korea

Material Description

Technical Data Sheet Compare

Technical Data Sheet