PC/ABS

PC/ABS CYCOLAC™ XCM830-76701 SABIC INNOVATIVE US

218

Unit Price:US$ 3,652 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
38MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜High impact resistance
Application Areas:Automotive interior parts｜Electrical applications
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C,TotalEnergy	ASTM D3763	65.0 J
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	45 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
elongation	Break3	ASTM D638	100 %
elongation	elongation	Break	ISO 527-2/5	100 %
Bending modulus	50.0mmSpan4	ASTM D790	3100 Mpa
Bending modulus	Bending modulus	--5	ISO 178	3100 Mpa
bending strength	--5,6	ISO 178	95.0 Mpa
bending strength	bending strength	Yield,50.0mmSpan4	ASTM D790	95.0 Mpa
Tensile modulus	--2	ASTM D638	3400 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	3100 Mpa
tensile strength	Yield3	ASTM D638	60.0 Mpa
	tensile strength	Yield	ISO 527-2/5	56.0 Mpa
		tensile strength	Break3	ASTM D638	55.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/5	55.0 Mpa
elongation	Yield3	ASTM D638	5.0 %
elongation	elongation	Yield	ISO 527-2/5	5.0 %

thermal performance	Test Condition	Test Method	Test Result
thermal conductivity		ISO 8302	0.20 W/m/K
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	118 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan9	ISO 75-2/Af	118 °C
Vicat softening temperature	--	ASTMD152510	138 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	140 °C
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	7E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	260°C/5.0kg	ASTM D1238	11 g/10min
Melt Volume Flow Rate (MVR)	260°C/5.0kg	ISO 1133	9.00 cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.70-0.80 %
Water absorption rate	Saturation,23°C	ISO 62	0.40 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.10 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/ABS CYCOLAC™ XCM830-76701 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet