LLDPE

LLDPE DOWLEX™ 2645.11G DOW USA

405

Unit Price:US$ 1,235 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
25MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Thin film grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
turbidity	50.8μm	ASTM D1003	14 %
gloss	45°,50.8μm	ASTM D2457	56
gloss	gloss	45°，50.8um	ASTM D-2457	56
turbidity	50.8um	ASTM D-1003	14 %

Other performance	Test Condition	Test Method	Test Result
Thin film puncture strength	50.8um	Internal Method	6.62 J/cm³

Basic Performance	Test Condition	Test Method	Test Result
film thickness			50.8 um
density		ASTM D-792	0.921 g/m3
melt mass-flow rate	190℃/2.16kg	ASTM D-1238	0.9 g/10min

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	50.8um，MD,Break	ASTM D-882	48.8 Mpa
	tensile strength	50.8um，TD,Break	ASTM D-882	39.2 Mpa
		tensile strength	50.8um，Yield,MD	ASTM D-882	14.2 Mpa
		tensile strength	tensile strength	50.8um，Yield,TD	ASTM D-882	14.6 Mpa
Secant modulus	2% Secant，50.8um，TD	ASTM D-882	238 Mpa
Secant modulus	Secant modulus	2% Secant，50.8um，MD	ASTM D-882	168 Mpa
Dart impact	50.8um	ASTM D-1709A	300 g
Elmendorf tear strength	50.8um，MD	ASTM D-1922	720 g
Elmendorf tear strength	Elmendorf tear strength	50.8um，TD	ASTM D-1922	1000 g

thermal performance	Test Condition	Test Method	Test Result
Melting temperature		Internal Method	120 °C
Vicat softening temperature		ASTM D1525	107 °C
Vicat softening temperature	Vicat softening temperature		ASTM D-1525	107 °C
Melting temperature		Internal Method	120 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	190°C/2.16kg	ASTM D1238	0.90 g/10min

film	Test Condition	Test Method	Test Result
Thin film puncture strength	51μm	Internal Method	6.62 J/cm³
film thickness			51 µm
Elmendorf tear strength	MD:51μm	ASTM D1922	720 g
Dart impact	51μm	ASTM D1709A	300 g
elongation	TD:Break,51μm	ASTM D882	740 %
elongation	elongation	MD:Break,51μm	ASTM D882	660 %
tensile strength	TD:Break,51μm	ASTM D882	39.2 Mpa
	tensile strength	MD:Break,51μm	ASTM D882	48.8 Mpa
		tensile strength	TD:Yield,51μm	ASTM D882	14.6 Mpa
		tensile strength	tensile strength	MD:Yield,51μm	ASTM D882	14.2 Mpa
Secant modulus	2%Secant,TD:51μm	ASTM D882	238 Mpa
Secant modulus	Secant modulus	2%Secant,MD:51μm	ASTM D882	168 Mpa
Elmendorf tear strength	TD:51μm	ASTM D1922	1000 g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

LLDPE DOWLEX™ 2645.11G DOW USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet