PC PANLITE® MN-3600HA TEIJIN JAPAN

445

Unit Price:US$ 2,233 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
31MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:heat-resisting｜Flame retardant｜Good impact resistance｜Good liquidity｜Halogen-free
Application Areas:Electrical field｜Electronic field｜Automotive sector
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179	NoBreak

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.45mm	UL 94	HB
	UL flame retardant rating	1.0mm	UL 94	V-1
		UL flame retardant rating	1.5mm	UL 94	V-0
			UL flame retardant rating	2.0mm	UL 94	5VB
			UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	5VA
Burning wire flammability index	1.0mm	IEC 60695-2-12	960 °C
	Burning wire flammability index	1.5mm	IEC 60695-2-12	930 °C
		Burning wire flammability index	2.0mm	IEC 60695-2-12	960 °C
		Burning wire flammability index	Burning wire flammability index	3.0mm	IEC 60695-2-12	930 °C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	875 °C
	Hot filament ignition temperature	1.5mm	IEC 60695-2-13	825 °C
		Hot filament ignition temperature	2.0mm	IEC 60695-2-13	825 °C
		Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	825 °C

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	95.0 Mpa
Tensile modulus		ISO 527-2/1	2350 Mpa
tensile strength	Yield	ISO 527-2/50	60.0 Mpa
tensile strength	tensile strength	Break	ISO 527-2/50	60.0 Mpa
Tensile strain	Yield	ISO 527-2/50	8.0 %
Tensile strain	Tensile strain	Break	ISO 527-2/50	100 %
Bending modulus		ISO 178	2300 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	126 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	113 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	7E-05 cm/cm/°C
RTI Elec	1.5mm	UL 746	95.0 °C
RTI Imp	1.5mm	UL 746	95.0 °C
RTI Str	1.5mm	UL 746	95.0 °C

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	280°C/5.0kg	ISO 1133	21.0 cm3/10min
Shrinkage rate	TD:4.00mm	Internal Method	0.50-0.70 %
Shrinkage rate	Shrinkage rate	MD:4.00mm	Internal Method	0.50-0.70 %
Water absorption rate	23°C,24hr	ISO 62	0.22 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	>1.0E+15 ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC PANLITE® MN-3600HA TEIJIN JAPAN

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet