Material Description

Material Properties:High mobility｜Good demolding performance｜Good forming performance
Application Areas:chip｜container｜Thin walled products｜Safety equipment｜Optical data storage｜lens
Color:--
Grade:Injection grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
Refractive index		ASTM D542	1.586
transmissivity	2540 μm	ASTM D1003	88.0 %
turbidity	2540 μm	ASTM D1003	1.0 %

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	12 kJ/m²
Suspended wall beam without notch impact strength	23°C	ASTM D4812	3200 J/m
Dart impact	23°C, Energy at Peak	ASTM D3763	54.0 J
Dart impact	Dart impact	23°C	ASTM D3029	169 J
Impact strength of cantilever beam gap		ASTM D1822	378 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.1 mm	UL 94	V-2
Extreme Oxygen Index		ISO 4589-2	25 %

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--2	ASTM D638	2370 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2350 Mpa
tensile strength	Yield3	ASTM D638	62.0 Mpa
	tensile strength	Yield	ISO 527-2/50	63.0 Mpa
		tensile strength	Break3	ASTM D638	65.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	50.0 Mpa
elongation	Yield3	ASTM D638	6.0 %
	elongation	Yield	ISO 527-2/50	6.0 %
		elongation	Break3	ASTM D638	120 %
		elongation	elongation	Break	ISO 527-2/50	70 %
Bending modulus	50.0 mm Span4	ASTM D790	2300 Mpa
Bending modulus	Bending modulus	--5	ISO 178	2300 Mpa
bending strength	--5,6	ISO 178	90.0 Mpa
bending strength	bending strength	Yield, 50.0 mm Span4	ASTM D790	93.0 Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0 mg

injection	Test Condition	Test Method	Test Result
drying temperature			120 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 60 %
Temperature at the rear of the barrel			250 to 270 °C
Temperature in the middle of the barrel			260 to 280 °C
Temperature at the front of the material cylinder			270 to 295 °C
Spray nozzle temperature			265 to 290 °C
Processing (melt) temperature			270 to 295 °C
Mold temperature			70 to 95 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.025 to 0.076 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	137 °C
	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span11	ISO 75-2/Be	133 °C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	126 °C
			Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	126 °C
			Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span11	ISO 75-2/Ae	121 °C
Vicat softening temperature	--	ISO 306/B50	139 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	140 °C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	-40 to 95°C，Flow	ASTM E831	6.8E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	23 to 80°C，Flow	ISO 11359-2	7.0E-5 cm/cm/°C
specific heat		ASTM C351	1250 J/kg/°C
thermal conductivity	--	ASTM C177	0.19 W/m/K
thermal conductivity	thermal conductivity	--	ISO 8302	0.20 W/m/K
RTI Elec		UL 746	130 °C
RTI Imp		UL 746	130 °C
RTI		UL 746	130 °C

Physical properties	Test Condition	Test Method	Test Result
Specific volume		ASTM D792	0.830 cm³/g
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	25 g/10 min
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	23.0 cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70 %
Water absorption rate	24 hr	ASTM D570	0.15 %
	Water absorption rate	Equilibrium, 23°C	ASTM D570	0.35 %
	Water absorption rate	Water absorption rate	Equilibrium, 100°C	ASTM D570	0.58 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	> 1.0E+15 ohms
Volume resistivity	--	ASTM D257	> 1.0E+17 ohms·cm
Volume resistivity	Volume resistivity	--	IEC 60093	> 1.0E+15 ohms·cm
Dielectric strength	3.20 mm, in Air	ASTM D149	15 KV/mm
Dielectric strength	Dielectric strength	3.20 mm, in Oil	IEC 60243-1	17 KV/mm
Dielectric constant	60 Hz	ASTM D150	3.17
	Dielectric constant	50 kHz	ASTM D150	3.17
		Dielectric constant	1 MHz	ASTM D150	2.96
			Dielectric constant	50 Hz	IEC 60250	2.70
				Dielectric constant	60 Hz	IEC 60250	2.70
				Dielectric constant	Dielectric constant	1 MHz	IEC 60250	2.70
Dissipation factor	50 Hz	ASTM D150	9.0E-4
	Dissipation factor	60 Hz	ASTM D150	9.0E-4
		Dissipation factor	1 MHz	ASTM D150	0.010
			Dissipation factor	50 Hz	IEC 60250	1.0E-3
			Dissipation factor	Dissipation factor	60 Hz	IEC 60250	1.0E-3
Compared to the anti leakage trace index		UL 746	PLC 2
High arc combustion index		UL 746	PLC 1
High voltage arc tracing rate		UL 746	PLC 2
Hot wire ignition		UL 746	PLC 2

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Scale	ASTM D785	70
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LEXAN™ HF1140 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet