PBT

PBT VALOX™ V2000DM SABIC INNOVATIVE NANSHA

Unit Price:US$ 3,297 /MT
Packaging Specification:
Supply Quantity:
33MT
Delivery Terms:
DDP
:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High rigidity｜high strength
Application Areas:Home appliance components｜Automotive Applications
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.0 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	2.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.0 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ASTM D4812	NoBreak
Dart impact	23°C,TotalEnergy	ASTM D3763	54.0 J

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ISO 527-2/50	59.0 Mpa
	tensile strength	Break	ASTM D638	40.0 Mpa
	tensile strength	tensile strength	Break	ISO 527-2/50	55.0 Mpa
elongation	Yield	ASTM D638	20 %
Tensile strain	Yield	ISO 527-2/50	7.0 %
elongation	Break	ASTM D638	100 %
Tensile strain	Break	ISO 527-2/50	15 %
Bending modulus	50.0mmSpan	ASTM D790	2570 Mpa
Bending modulus	Bending modulus		ISO 178	2500 Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	90.0 Mpa
Tensile modulus		ASTM D638	2810 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	3000 Mpa
tensile strength	Yield	ASTM D638	59.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature	--	ISO 306/B120	185 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	8.4E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	8.4E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	8E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	8E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	54.0 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	53.0 °C
Vicat softening temperature		ASTM D15259	185 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	186 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	250°C/2.16kg	ASTM D1238	35 g/10min
Melt Volume Flow Rate (MVR)	250°C/2.16kg	ISO 1133	34.0 cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	2.1-2.4 %
Water absorption rate	Saturation,23°C	ISO 62	0.080 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.34 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT VALOX™ V2000DM SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet Compare

Technical Data Sheet