PC INFINO® HN-3104-K2495 Samsung Cheil South Korea

184

Unit Price:US$ 3,483 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜Flame retardant｜Filler: Glass fiber reinforced material
Application Areas:smart meter ｜Wiring equipment
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	10 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	10 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-0
Burning wire flammability index	1.6mm	IEC 60695-2-12	960 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	3400 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/5	3500 Mpa
tensile strength	Yield	ASTM D638	54.0 Mpa
	tensile strength	Yield	ISO 527-2/5	60.0 Mpa
		tensile strength	Break	ASTM D638	54.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/5	60.0 Mpa
elongation	Break	ASTM D638	6.0 %
Tensile strain	Break	ISO 527-2/5	6.0 %
Bending modulus		ASTM D790	3400 Mpa
Bending modulus	Bending modulus		ISO 178	3500 Mpa
bending strength		ASTM D790	98.0 Mpa
bending strength	bending strength		ISO 178	90.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	139 °C
	Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	136 °C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	140 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	137 °C
Vicat softening temperature		ISO 306/B50	136135 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	250°C/10.0kg	ASTM D1238	13 g/10min
	melt mass-flow rate	260°C/5.0kg	ASTM D1238	8.0 g/10min
		melt mass-flow rate	250°C/10.0kg	ISO 1133	13 g/10min
		melt mass-flow rate	melt mass-flow rate	260°C/5.0kg	ISO 1133	8.0 g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	0.10-0.20 %
	Shrinkage rate	TD：3.20mm	ASTM D955	0.10-0.20 %
		Shrinkage rate	TD:3.20mm	ISO 2577	0.10-0.20 %
		Shrinkage rate	Shrinkage rate	MD:3.20mm	ISO 2577	0.10-0.20 %
ash content	--	ISO 3451	11 %
ash content	ash content	--	ASTM D5630	11 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	115
Rockwell hardness	Rockwell hardness	R-Scale	ISO 2039-2	115

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.