PBT CELANEX® 2300GV1/20 CELANESE USA

246

Unit Price:US$ 3,796 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High toughness｜Hydrolysis resistance｜Thermal stability｜Weather resistance｜UV resistance
Application Areas:Automotive Applications
Color:--
Grade:--

Technical Data Sheet

Filling analysis	Test Method	Test Result
Density of Melt	Internal Method	1.230 g/cm³
SpecificHeatCapacity of Melt	Internal Method	1840 J/kg/°C
ThermalConductivityofMelt	Internal Method	0.16 W/m/K

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	46 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	43 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.2mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	HB
Extreme Oxygen Index		ISO 4589-2	20 %

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1A/1	7400 Mpa
tensile strength	Break	ISO 527-2/1A/5	125 Mpa
Tensile strain	Break	ISO 527-2/1A/5	3.0 %
Tensile creep modulus	1hr	ISO 899-1	6200 Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	4800 Mpa
bending strength	23°C	ISO 178	170 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	220 °C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	195 °C
	Hot deformation temperature	Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	100 °C
Vicat softening temperature		ISO 306/B50	215 °C
Melting temperature		ISO 11357-3	225 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	3.5E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15 %
Melt Volume Flow Rate (MVR)	250°C/2.16kg	ISO 1133	14.0 cm3/10min
Shrinkage rate	TD	ISO 294-4	1.0-1.3 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.40-0.50 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Dielectric strength		IEC 60243-1	31 KV/mm
Relative permittivity	100Hz	IEC 60250	4.20
Relative permittivity	Relative permittivity	1MHz	IEC 60250	4.10
Dissipation factor	100Hz	IEC 60250	1.6E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.019
Compared to the anti leakage trace index		IEC 60112	PLC 2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.