POM

POM LNP™ LUBRICOMP™ KD000 BKANT SABIC INNOVATIVE US

259

Unit Price:US$ 3,692 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
49.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:heat-resisting｜high strength｜Glass fiber reinforced
Application Areas:Automotive Applications
Color:--
Grade:Extrusion grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Multi axis Instrumented Impact Energy		ISO 6603-2	1.50 J
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	5.00 J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	37 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.70mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	82.0 Mpa
bending strength	bending strength		ASTM D790	95.0 Mpa
Bending modulus		ISO 178	3200 Mpa
Bending modulus	Bending modulus		ASTM D790	3250 Mpa
Tensile strain	Break	ISO 527-2	20 %
elongation	Break	ASTM D638	7.2 %
Tensile strain	Yield	ISO 527-2	5.0 %
elongation	Yield	ASTM D638	3.6 %
Tensile modulus		ASTM D638	3500 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	3000 Mpa
tensile strength	Yield	ASTM D638	58.0 Mpa
	tensile strength	Yield	ISO 527-2	53.0 Mpa
		tensile strength	Break	ASTM D638	54.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2	47.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	1E-04 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	1E-04 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	1E-04 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	105 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	108 °C
Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	1E-04 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD：24hr	ASTM D955	1.5-3.5 %
	Shrinkage rate	TD：100°C	Internal Method	1.1-1.2 %
		Shrinkage rate	TD：60°C	Internal Method	0.90-1.0 %
			Shrinkage rate	MD：24hr	ASTM D955	1.5-3.5 %
				Shrinkage rate	MD：100°C	Internal Method	1.5-1.6 %
					Shrinkage rate	MD：60°C	Internal Method	1.2-1.3 %
						Shrinkage rate	TD:24hr	ISO 294-4	1.5-3.5 %
						Shrinkage rate	Shrinkage rate	MD:24hr	ISO 294-4	1.5-3.5 %
Water absorption rate	24hr,50%RH	ASTM D570	0.28 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.33 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		ASTM D257	1.0E+2to1.0E+4 ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

POM LNP™ LUBRICOMP™ KD000 BKANT SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet