PA6T

PA6T Zytel® FR52G20NH DUPONT USA

323

Unit Price:US$ 7,560 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜High temperature resistance｜Filler: Glass fiber reinforced material｜20% filler by weight
Application Areas:Electronic and electrical components
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	kJ/m²	40
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	kJ/m²	40

flammability	Test Condition	Test Method	Test Result
Flammability level	0.750mm		V-0 --
Flammability level	Flammability level	1.50mm		V-0 --
Burning wire flammability index	0.400mm	°C	960 --
Hot filament ignition temperature	0.400mm	°C	725 --
Extreme Oxygen Index		%	35 --

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus			8200 MPa
tensile strength	Break		135 MPa
Tensile strain	Break	%	2.4 2.2
Bending modulus		MPa	7800 8200
bending strength		MPa	215 180

thermal performance	Test Condition	Test Method	Test Result
Melting temperature		°C	310 --
Linear coefficient of thermal expansion	MD	cm/cm/°C	2.5E-05 --
	Linear coefficient of thermal expansion	MD:-40to23°C	cm/cm/°C	2.7E-05 --
		Linear coefficient of thermal expansion	MD:55to160°C	cm/cm/°C	2.1E-05 --
			Linear coefficient of thermal expansion	TD	cm/cm/°C	6.8E-05 --
				Linear coefficient of thermal expansion	TD:-40to23°C	cm/cm/°C	6.4E-05 --
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:55to160°C	cm/cm/°C	1E-04 --
Hot deformation temperature	1.8MPa,Unannealed	°C	276 --

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD	%	1.1 --
Shrinkage rate	Shrinkage rate	MD	%	0.30 --

Electrical performance	Test Method	Test Result
Volume resistivity	ohms·cm	>1.0E+15 --
Dielectric strength	kV/mm	42 --
Compared to the anti leakage trace index	V	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.