PC/ABS

PC/ABS CYCOLOY™ 7210A-BK1D588 SABIC INNOVATIVE NANSHA

223

Unit Price:US$ 3,758 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜High impact resistance｜Filler: Talc filler
Application Areas:Automotive interior parts｜Electrical applications｜Thin walled components
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C,TotalEnergy	ASTM D3763	47.5 J
Suspended wall beam without notch impact strength	23°C	ASTM D4812	1900 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.98mm	UL 94	5VB
UL flame retardant rating	UL flame retardant rating	1.19mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Break,50.0mmSpan	ASTM D790	106 Mpa
Bending modulus	50.0mmSpan	ASTM D790	3140 Mpa
elongation	Break	ASTM D638	80 %
elongation	elongation	Yield	ASTM D638	3.6 %
tensile strength	Break	ASTM D638	49.0 Mpa
tensile strength	tensile strength	Yield	ASTM D638	63.4 Mpa
Tensile modulus		ASTM D638	3520 Mpa

thermal performance	Test Condition	Test Method	Test Result
RTI Elec		UL 746	90.0 °C
Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	6.7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	5.9E-05 cm/cm/°C
Vicat softening temperature		ASTM D15256	102 °C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	82.2 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	92.2 °C
RTI		UL 746	90.0 °C
RTI Imp		UL 746	85.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD:3.20mm	Internal Method	0.40-0.60 %
Shrinkage rate	Shrinkage rate	MD:3.20mm	Internal Method	0.30-0.50 %
melt mass-flow rate	260°C/2.16kg	ASTM D1238	16 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/ABS CYCOLOY™ 7210A-BK1D588 SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet Compare

Technical Data Sheet