UHMWPE

UHMWPE GUR® 4130 CELANESE USA

403

Unit Price:US$ 3,689 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
109.1MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Ultra high molecular weight｜Good impact resistance｜Lubricity｜Low friction coefficient｜wear resistant
Application Areas:Automotive Applications｜transportation industry
Color:--
Grade:Withdrawal level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength		ISO 1152-2	210 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ASTM D638	703 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1A/1	640 Mpa
tensile strength	Yield,23°C	ASTM D638	21.4 Mpa
tensile strength	tensile strength	Yield	ISO 527-2/1A/50	19.0 Mpa
Tensile strain	Yield	ISO 527-2/1A/50	14 %
Tensile strain	Tensile strain	Break,23°C	ASTM D638	>350 %
Nominal tensile fracture strain		ISO 527-2/1A/50	>50 %
Tensile creep modulus	1hr	ISO 899-1	430 Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	230 Mpa
Friction coefficient	Steel - Dynamic	Internal Method	0.10
Wear factor	砂浆法	Internal Method	90.0
Wear amount		Internal Method	90.0

thermal performance	Test Condition	Test Method	Test Result
specific heat	23°C	Internal Method	1840 J/kg/°C
thermal conductivity	23°C	Internal Method	0.41 W/m/K
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	65.0 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	38.0 °C
Vicat softening temperature		ASTMD1525	80.0 °C
Linear coefficient of thermal expansion	MD	ASTMD696	2E-04 cm/cm/°C

Physical properties	Test Method	Test Result
Stickiness	ISO 307	3000 cm³/g
Elongation at Break	ISO 1152-2	0.380 Mpa
Intrinsic viscosity	ISO 1628-3	25 dl/g

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	100Hz	IEC 60250	3.9E-04
Dissipation factor	Dissipation factor	1MHz	IEC 60250	1E-03
Compared to the anti leakage trace index		IEC 60112	PLC 0
Surface resistivity	--	ASTM D257	>1.0E+13 ohms
Surface resistivity	Surface resistivity	--	IEC 60093	>1.0E+12 ohms
Volume resistivity	--	ASTM D257	>1.0E+15 ohms·cm
Volume resistivity	Volume resistivity	--	IEC 60093	>1.0E+14 ohms·cm
Dielectric strength		IEC 60243-1	45 KV/mm
Dielectric constant	1MHz	ASTM D150	3.00
	Dielectric constant	100Hz	IEC 60250	2.00
	Dielectric constant	Dielectric constant	1MHz	IEC 60250	2.00

hardness	Test Condition	Test Method	Test Result
Shore hardness	ShoreD	ASTM D2240	62
Shore hardness	Shore hardness	ShoreD,15Sec	ISO 868	60
Ball Pressure Test		ISO 2039-1	35.0 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

UHMWPE GUR® 4130 CELANESE USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet