PC Makrolon® RX1805 COVESTRO THAILAND

389

Unit Price:US$ 7,229 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:transparent
Application Areas:Medical supplies
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	-30°C,Complete Break	ISO 7391	15 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Charpy Notched Impact Strength	23°C,Partial Break	ISO 7391	80 kJ/m²
Impact strength of simply supported beam without notch	-60°C	ISO 179/1eU	NoBreak
Charpy Notched Impact Strength	-30°C,Complete Break	ISO 7391	16 kJ/m²
Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	5700 N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force	-30°C	ISO 6603-2	6600 N
Impact strength of cantilever beam gap	23°C,Partial Break	ISO 7391	70 kJ/m²
Multi axis Instrumented Impact Energy	-30°C	ISO 6603-2	70.0 J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	65.0 J

flammability	Test Method	Test Result
SelfIgnition	ASTM D1929	550 °C
Extreme Oxygen Index	ISO 4589-2	27 %
FlashIgnitionTemperature	ASTM D1929	480 °C

mechanical properties	Test Condition	Test Method	Test Result
bending strength	23°C	ISO 178	98.0 Mpa
Bending strain	23°C	ISO 178	7.1 %
bending strength	3.5%Strain,23°C	ISO 178	73.0 Mpa
Nominal tensile fracture strain	23°C	ISO 527-2/50	>50 %
Bending modulus	23°C	ISO 178	2400 Mpa
Tensile strain	Break,23°C	ISO 527-2/50	130 %
Tensile strain	Tensile strain	Yield,23°C	ISO 527-2/50	6.3 %
tensile strength	Yield,23°C	ISO 527-2/50	67.0 Mpa
tensile strength	tensile strength	Break,23°C	ISO 527-2/50	75.0 Mpa
Tensile modulus	23°C	ISO 527-2/1	2400 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature	--	ISO 306/B50	144 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	138 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	126 °C
Glass transition temperature		ISO 11357-2	145 °C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	6.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	6.5E-05 cm/cm/°C
thermal conductivity	23°C	ISO 8302	0.20 W/m/K
Vicat softening temperature	--	ISO 306/B120	145 °C
Ball Pressure Test	135°C	IEC 60695-10-2	Pass

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD	ISO 2577	0.60-0.80 %
Shrinkage rate	Shrinkage rate	TD	ISO 2577	0.60-0.80 %
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	6.00 cm3/10min
Apparent density		ISO 60	0.66 g/cm³
melt mass-flow rate	300°C/1.2kg	ISO 1133	6.5 g/10min
density	23°C	ISO 1183	1.20 g/cm³
Water absorption rate	Saturation,23°C	ISO 62	0.30 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.12 %
Shrinkage rate	TD:2.00mm3	ISO 294-4	0.70 %
Shrinkage rate	Shrinkage rate	MD:2.00mm3	ISO 294-4	0.70 %

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test		ISO 2039-1	114 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.