PC LEXAN™ LUX9612 SABIC INNOVATIVE NANSHA

209

Unit Price:US$ 4,546 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
18.8MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:optical performance ｜UV resistance｜Weather resistance｜transparent｜Flame retardant
Application Areas:Lighting applications｜Home appliance components｜Automotive sector
Color:--
Grade:Light diffusion level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
23°C		ASTM D256	400 J/m
23°C	23°C		ISO 180/1A	40 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	70.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.50mm	UL 94	V-0
Burning wire flammability index	1.00mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.00mm	IEC 60695-2-13	850 °C
Hot filament ignition temperature	Hot filament ignition temperature	1.50mm	IEC 60695-2-13	850 °C

mechanical properties	Test Condition	Test Method	Test Result
--1		ASTM D638	2300 Mpa
yield		ASTM D638	62.0 Mpa
Yield, 50.0mm span		ASTM D790	95.0 Mpa
yield		ISO 527-2/50	62.0 Mpa
crack		ASTM D638	65.0 Mpa
crack	crack		ISO 527-2/50	58.0 Mpa
yield		ASTM D638	6.0 %
yield	yield		ISO 527-2/50	6.0 %
crack		ASTM D638	80 %
crack	crack		ISO 527-2/50	75 %
50.0mm span		ASTM D790	2160 Mpa
--7		ISO 178	2250 Mpa
--8		ISO 178	95.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
0.45MPa, unannealed, 64.0mm span		ISO 75-2/Bf	135 °C
1.8MPa, unannealed, 3.20mm		ASTM D648	123 °C
1.8MPa, unannealed, 64.0mm span of		ISO 75-2/Af	123 °C
Vicat softening temperature		ASTM D152513	140 °C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	6.8E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	6.7E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	300°C/1.2kg	ASTM D1238	7.0 g/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.60-0.80 %
Water absorption rate	Saturation,23°C	ISO 62	0.35 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	CTI	UL 746	PLC 3
High arc combustion index	HAI	UL 746	PLC 1
Hot wire ignition	HWI	UL 746	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LEXAN™ LUX9612 SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet Compare

Technical Data Sheet