PC LEXAN™  EXL1433T SABIC INNOVATIVE NANSHA

204
  • Unit Price:US$ 5,445 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    52.3MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Middle flow｜High ductility at low temperature｜Short molding cycle
  • Application Areas:Automotive sector｜Electronic and Electrical Applications｜Plastic bag
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

optical performanceTest ConditionTest MethodTest Result
transmissivity2540μmASTM D100382.0 %
turbidity2540μmASTM D10033.0 %
impact performanceTest ConditionTest MethodTest Result
Dart impact-30°C,TotalEnergyASTM D376385.0 J
Dart impact23°C,TotalEnergyASTM D376382.4 J
Charpy Notched Impact Strength-30°CISO 179/1eA50 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA70 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap-30°CISO 180/1A45 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A65 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1UNoBreak
Suspended wall beam without notch impact strength23°CISO 180/1UNoBreak
-30°CISO 180/1A45 kJ/m²
23°CISO 180/1A65 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Charpy Notched Impact Strength-30°CISO 179/1eA50 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA70 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
-30°CASTM D256800 J/m
23°CASTM D256890 J/m
flammabilityTest ConditionTest MethodTest Result
Hot filament ignition temperature0.8mmIEC 60695-2-13825 °C
Hot filament ignition temperature3.0mmIEC 60695-2-13825 °C
UL flame retardant rating2.5mmUL 94V-2
UL flame retardant rating3.0mmUL 94V-2
Burning wire flammability index3.0mmIEC 60695-2-12960 °C
UL flame retardant rating2.50mmUL 94V-2
Burning wire flammability index3.00mmIEC 60695-2-12960 °C
Hot filament ignition temperature0.800mmIEC 60695-2-13825 °C
Hot filament ignition temperature3.00mmIEC 60695-2-13825 °C
mechanical propertiesTest ConditionTest MethodTest Result
Bending modulusISO 1782150 Mpa
bending strengthISO 17890.2 Mpa
bending strengthYield,50.0mmSpanASTM D79094.3 Mpa
Tensile modulusISO 527-2/12350 Mpa
tensile strengthYieldASTM D63858.0 Mpa
tensile strengthYieldISO 527-2/5057.9 Mpa
tensile strengthBreakASTM D63864.1 Mpa
tensile strengthBreakISO 527-2/5061.5 Mpa
elongationYieldASTM D6385.8 %
Tensile strainYieldISO 527-2/505.5 %
elongationBreakASTM D638130 %
Tensile strainBreakISO 527-2/50120 %
Bending modulus50.0mmSpanASTM D7902220 Mpa
Tensile modulusASTM D6382220 Mpa
50.0mm spanASTM D7902220 Mpa
--7ISO 1782150 Mpa
--8ISO 17890.2 Mpa
Yield, 50.0mm spanASTM D79094.3 Mpa
--1ASTM D6382220 Mpa
yieldASTM D63858.0 Mpa
yieldISO 527-2/5057.9 Mpa
crackASTM D63864.1 Mpa
crackISO 527-2/5061.5 Mpa
yieldASTM D6385.8 %
yieldISO 527-2/505.5 %
crackASTM D638130 %
crackISO 527-2/50120 %
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648124 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af119 °C
Vicat softening temperatureASTM D152510141 °C
Vicat softening temperature--ISO 306/B50141 °C
Vicat softening temperature--ISO 306/B120142 °C
Ball Pressure Test125°CIEC 60695-10-2Pass
Linear coefficient of thermal expansionMD：-40to95°CASTME8317.2E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：23to80°CISO 11359-27.2E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to95°CASTME8317.9E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：23to80°CISO 11359-27.9E-05 cm/cm/°C
RTI ElecUL 746130 °C
RTI StrUL 746130 °C
1.8MPa, unannealed, 3.20mmASTM D648124 °C
1.8MPa, unannealed, 64.0mm span ofISO 75-2/Af119 °C
Flow: -40 to 95 ° C-40to95℃ASTME8317.2E-05 cm/cm/°C
Flow: 23 to 80 ° C23to80℃ISO 11359-27.2E-05 cm/cm/°C
Horizontal: -40 to 95 ° CAcross Flow, -40to95℃ASTME8317.9E-05 cm/cm/°C
Horizontal: 23 to 80 ° CAcross Flow, 23to80℃ISO 11359-27.9E-05 cm/cm/°C
RTIUL 746130 °C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate300°C/1.2kgASTM D123810 g/10min
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11339.50 cm3/10min
Shrinkage rateMD：3.20mmInternal Method0.40-0.80 %
Shrinkage rateTD：3.20mmInternal Method0.40-0.80 %
Water absorption rateSaturation,23°CISO 620.12 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.093 %
Shrinkage rateMD:3.20mmInternal Method0.40-0.80 %
Shrinkage rateTD:3.20mmInternal Method0.40-0.80 %
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityASTM D257>1.0E+15 ohms
Volume resistivityASTM D257>1.0E+15 ohms·cm
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessL-SaleASTM D78590
Rockwell hardnessL-SaleISO 2039-290
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.