Material Description

Material Properties:Thermal stability｜High temperature resistance
Application Areas:Electrical applications｜Lighting applications
Color:--
Grade:Injection grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
Refractive index		ISO 489	1.586
transmissivity	2540μm	ASTM D1003	88.0 %

impact performance	Test Condition	Test Method	Test Result
-30°C		ASTM D256	110 J/m
23°C		ASTM D256	650 J/m
-30°C		ISO 180/1A	11 kJ/m²
23°C		ISO 180/1A	65 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
23°C		ISO 179/2C	11 kJ/m²
23°C	23°C		ISO 179/1eA	65 kJ/m²
-30°C		ISO 179/1eA	12 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Dart impact	23°C,TotalEnergy	ASTM D3763	60.0 J
Charpy Notched Impact Strength	23°C	ISO 179/1eA	65 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	12 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	V-2
	UL flame retardant rating	3.0mm	UL 94	V-0
		UL flame retardant rating	3.00mm	UL 94	V-0
		UL flame retardant rating	UL flame retardant rating	1.50mm	UL 94	V-2

mechanical properties	Test Condition	Test Method	Test Result
Yield, 50.0mm span		ASTM D790	95.0 Mpa
yield		ASTM D638	66.0 Mpa
--2		ASTM D638	2400 Mpa
--9		ISO 178	98.0 Mpa
--8		ISO 178	2400 Mpa
50.0mm span		ASTM D790	2400 Mpa
crack		ISO 527-2/50	100 %
crack	crack		ASTM D638	100 %
yield		ISO 527-2/50	6.0 %
yield	yield		ASTM D638	6.0 %
crack		ISO 527-2/50	66.0 Mpa
crack	crack		ASTM D638	66.0 Mpa
yield		ISO 527-2/50	66.0 Mpa
elongation	Yield3	ASTM D638	6.0 %
elongation	elongation	Yield	ISO 527-2/50	6.0 %
Tensile modulus	--2	ASTM D638	2400 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2400 Mpa
tensile strength	Yield3	ASTM D638	66.0 Mpa
	tensile strength	Yield	ISO 527-2/50	66.0 Mpa
		tensile strength	Break3	ASTM D638	66.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	66.0 Mpa
elongation	Break	ISO 527-2/50	100 %
Bending modulus	50.0mmSpan4	ASTM D790	2400 Mpa
elongation	Break3	ASTM D638	100 %
Bending modulus	--5	ISO 178	2400 Mpa
bending strength	--5,6	ISO 178	98.0 Mpa
bending strength	bending strength	Yield,50.0mmSpan4	ASTM D790	95.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
0.45MPa, unannealed, 100mm span		ISO 75-2/Be	134 °C
1.8MPa, unannealed, 3.20mm		ASTM D648	125 °C
1.8MPa, unannealed, 100mm span		ISO 75-2/Ae	123 °C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	125 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,100mmSpan9	ISO 75-2/Ae	123 °C
Vicat softening temperature	--	ASTMD152510	140 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	141 °C
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	7E-05 cm/cm/°C
Flow: -40 to 40 ° C		ASTME831	7E-05 cm/cm/°C
Horizontal: -40 to 40 ° C	Across Flow, -40to40℃	ASTME831	7E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.35 %
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70 %
Shrinkage rate	Shrinkage rate	MD：--1	Internal Method	0.50-0.70 %
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	21.0 cm3/10min
melt mass-flow rate	300°C/1.2kg	ASTM D1238	23 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LEXAN™ 915AU SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet Compare

Technical Data Sheet