POM

POM Delrin® 570 BK DUPONT USA

240

Unit Price:US$ 3,189 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
80MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:UV resistance｜wear resistant｜High temperature resistance｜Filler: Glass fiber reinforced material｜20% filler by weight｜20% filler by weight
Application Areas:household electrical appliances｜Fitness equipment
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	3.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	3.5 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	50 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	54 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	6.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.0mm	UL 94	HB
	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
	UL flame retardant rating	UL flame retardant rating	3.0mm	IEC 60695-11-10,-20	HB
FMVSS flammability		FMVSS302	B
Fogging-G-value	condensate	ISO 6452	5E-04 g
Burning rate	1.00mm	ISO 3795	53 mm/min
UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	4900 Mpa
tensile strength	Break	ISO 527-2	53.0 Mpa
Tensile strain	Break	ISO 527-2	12 %
Bending modulus		ISO 178	4600 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	165 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	125 °C
Vicat softening temperature		ISO 306/B50	160 °C
Melting temperature		ISO 11357-3	178 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	8.5E-05 cm/cm/°C
AnnealingTemperature			160 °C
AnnealingTime-Optional			30.0 min/mm

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.56 g/cm³
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	7.00 cm3/10min
Shrinkage rate	TD	ISO 294-4	1.2 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	1.8 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	0.80 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.10 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		IEC 60093	1E+15 ohms·cm
Relative permittivity	100Hz	IEC 60250	3.90
Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.90
Compared to the anti leakage trace index		IEC 60112	V

Supplementary Information	Test Condition	Test Method	Test Result
Emission		VDA275	<8.00 mg/kg
EmissionofOrganicCompounds		VDA277	4.80 µgC/g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

POM Delrin® 570 BK DUPONT USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet