PC/ABS

PC/ABS CYCOLOY™ MC1300-GY6026 SABIC INNOVATIVE NANSHA

235

Unit Price:US$ 3,783 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance｜High mobility｜Easy electroplating
Application Areas:Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	-30°C, Total Energy	ASTM D3763	33.0 J
Dart impact	Dart impact	23°C, Total Energy	ASTM D3763	40.0 J

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	2130 Mpa
tensile strength	Yield	ASTM D638	50.0 Mpa
tensile strength	tensile strength	Break	ASTM D638	44.0 Mpa
elongation	Yield	ASTM D638	8.6 %
elongation	elongation	Break	ASTM D638	150 %
Bending modulus	50.0 mm Span	ASTM D790	2060 Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	72.0 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			100 to 105 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			30 to 80 %
Temperature at the rear of the barrel			250 to 280 °C
Temperature in the middle of the barrel			255 to 290 °C
Temperature at the front of the material cylinder			255 to 290 °C
Spray nozzle temperature			260 to 290 °C
Processing (melt) temperature			260 to 290 °C
Mold temperature			75 to 100 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.038 to 0.076 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	115 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	98.0 °C
Vicat softening temperature		ASTM D15255	111 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.2E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	9.0E-5 cm/cm/°C
thermal conductivity		ASTM C177	0.20 W/m/K

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	260°C/5.0 kg	ASTM D1238	14 g/10 min
Shrinkage rate	Flow : 3.20 mm	Internal Method	0.50 - 0.80 %
Shrinkage rate	Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.50 - 0.70 %
Water absorption rate	24 hr	ASTM D570	0.10 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/ABS CYCOLOY™ MC1300-GY6026 SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet Compare

Technical Data Sheet