PC LEXAN™ EXL1330 WH SABIC INNOVATIVE US

204

Unit Price:US$ 4,045 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
15MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Middle flow｜Ductility at low temperature｜Short molding cycle
Application Areas:sporting goods｜Aerospace Applications｜Electrical appliances｜Plastic bag
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	60 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C	ISO 179/1eA	75 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Dart impact	23°C, Total Energy	ASTM D3763	52.0 J

flammability	Test Condition	Test Method	Test Result
Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	875 °C
Extreme Oxygen Index		ISO 4589-2	35 %
UL flame retardant rating	0.8 mm	UL 94	HB
Burning wire flammability index	0.8 mm	IEC 60695-2-12	850 °C
Burning wire flammability index	Burning wire flammability index	1.0 mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	875 °C

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield, 50.0 mm Span4	ASTM D790	88.0 Mpa
bending strength	bending strength	--5,6	ISO 178	85.0 Mpa
Bending modulus	--5	ISO 178	2100 Mpa
Bending modulus	Bending modulus	50.0 mm Span4	ASTM D790	2060 Mpa
elongation	Break	ISO 527-2/50	> 100 %
	elongation	Break3	ASTM D638	130 %
		elongation	Yield	ISO 527-2/50	5.0 %
		elongation	elongation	Yield3	ASTM D638	6.0 %
tensile strength	Break	ISO 527-2/50	56.0 Mpa
	tensile strength	Break3	ASTM D638	61.0 Mpa
		tensile strength	Yield	ISO 527-2/50	55.0 Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	58.0 Mpa
Tensile modulus	--	ISO 527-2/1	2100 Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	2100 Mpa

injection	Test Condition	Test Method	Test Result
drying time			3.0 to 4.0 hr
drying temperature			120 °C
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 60 %
Temperature at the rear of the barrel			215 to 295 °C
Temperature in the middle of the barrel			280 to 305 °C
Temperature at the front of the material cylinder			295 to 315 °C
Spray nozzle temperature			290 to 310 °C
Processing (melt) temperature			295 to 315 °C
Mold temperature			70 to 95 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.025 to 0.076 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	134 °C
	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span10	ISO 75-2/Be	136 °C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	120 °C
			Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	124 °C
			Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span10	ISO 75-2/Ae	125 °C
Vicat softening temperature	--	ASTM D152511	143 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	145 °C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	6.7E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	7.2E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	6.7E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	7.2E-5 cm/cm/°C
RTI Elec		UL 746	125 °C
RTI Imp		UL 746	115 °C
RTI		UL 746	120 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.15 %
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.35 %
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.40 - 0.80 %
Shrinkage rate	Shrinkage rate	Flow : 3.20 mm	Internal Method	0.40 - 0.80 %
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	9.00 cm3/10min
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	10 g/10 min

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test	H 358/30	ISO 2039-1	90.0 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.