Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:--

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
transmissivity	2540μm	ASTM D1003	82.0 %
turbidity	2540μm	ASTM D1003	3.0 %

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	60 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	70 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	-30°C	ASTM D256	710 J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	820 J/m
		Impact strength of cantilever beam gap	-30°C9	ISO 180/1A	55 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C9	ISO 180/1A	65 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Dart impact	-30°C,TotalEnergy	ASTM D3763	77.4 J
Dart impact	Dart impact	23°C,TotalEnergy	ASTM D3763	75.5 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-2
Burning wire flammability index	3.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	0.8mm	IEC 60695-2-13	850 °C
Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	850 °C

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield4	ASTM D638	57.6 Mpa
	tensile strength	Yield	ISO 527-2/50	56.8 Mpa
		tensile strength	Break4	ASTM D638	59.1 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	55.3 Mpa
elongation	Yield4	ASTM D638	5.6 %
	elongation	Yield	ISO 527-2/50	5.4 %
		elongation	Break4	ASTM D638	120 %
		elongation	elongation	Break	ISO 527-2/50	110 %
Bending modulus	50.0mmSpan5	ASTM D790	2180 Mpa
Bending modulus	Bending modulus	--6	ISO 178	2120 Mpa
bending strength	--6,7	ISO 178	88.6 Mpa
bending strength	bending strength	Yield,50.0mmSpan5	ASTM D790	92.0 Mpa
Tensile modulus	--3	ASTM D638	2190 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2310 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD:23to80°C	ISO 11359-2	6.7E-05 cm/cm/°C
	Linear coefficient of thermal expansion	TD:-40to95°C	ASTME831	8E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to80°C	ISO 11359-2	8E-05 cm/cm/°C
RTI Elec		UL 746	130 °C
RTI		UL 746	130 °C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	121 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan10	ISO 75-2/Af	116 °C
Vicat softening temperature	--	ASTMD152511	139 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	138 °C
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	MD:-40to95°C	ASTME831	6.7E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
density		ASTMD792	1.19 g/cm³
melt mass-flow rate	300°C/1.2kg	ASTM D1238	10 g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	9.50 cm3/10min
Shrinkage rate	MD:3.20mm	Internal Method	0.40-0.80 %
Shrinkage rate	Shrinkage rate	TD:3.20mm	Internal Method	0.40-0.80 %
Water absorption rate	Saturation,23°C	ISO 62	0.12 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.093 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		ASTM D257	>1.0E+15 ohms
Volume resistivity		ASTM D257	>1.0E+15 ohms·cm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	L-Sale	ISO 2039-2	87

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC EXL1414T-NA8A005T SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet Compare

Technical Data Sheet