ABS

ABS CYCOLAC™ BDT5510-1000 SABIC INNOVATIVE US

227

Unit Price:US$ 3,506 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Low gloss
Application Areas:Automotive sector｜Automotive interior parts
Color:--
Grade:Injection grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
gloss	60°,无织构	ASTM D523	25

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	7.2 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	13 kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256	290 J/m
	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	7.0 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	13 kJ/m²
Dart impact	23°C	ASTM D3029	35.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		ISO 178	2030 Mpa
bending strength		ISO 178	67.0 Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	81.0 Mpa
Tensile modulus		ASTM D638	2280 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	2930 Mpa
tensile strength	Yield	ASTM D638	53.0 Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	43.0 Mpa
Bending modulus	50.0mmSpan	ASTM D790	2460 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	92.0 °C
	Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	95.0 °C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	81.0 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	83.0 °C
Vicat softening temperature		ISO 306/B50	98.0 °C
Linear coefficient of thermal expansion	MD：-40to60°C	ASTME831	1.4E-04 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Melt viscosity	260°C,1000sec^-1	ASTM D3835	163 Pa·s
density		ASTM D792	1.05 g/cm³
melt mass-flow rate	230°C/3.8kg	ASTM D1238	6.0 g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ISO 1133	14 g/10min
Spiral flow length		Internal Method	73.7 CM
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.80 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.