PC/ABS

PC/ABS MULTILON® TN-7000F TEIJIN JAPAN

244

Unit Price:US$ 2,483 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
31MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant
Application Areas:Electrical applications｜Computer components
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179	NoBreak

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.2mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	1.8mm	UL 94	5VB

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		ISO 178	3200 Mpa
bending strength		ISO 178	96 Mpa
Impact strength of cantilever beam gap	没Notched	ISO 179	NB KJ/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	带Notched	ISO 179	12 KJ/m
Tensile modulus		ISO 527-1	3300 Mpa
Tensile stress		ISO 527-1	63 Mpa
Tensile stress	Tensile stress	Break	ISO 527-1	46 Mpa
elongation at yield		ISO 527-1	2 %
Elongation at Break		ISO 527-1	20 %
Tensile modulus		ISO 527-2/1	3300 Mpa
tensile strength	Yield	ISO 527-2/50	63.0 Mpa
tensile strength	tensile strength	Break	ISO 527-2/50	46.0 Mpa
Tensile strain	Yield	ISO 527-2/50	2.0 %
Tensile strain	Tensile strain	Break	ISO 527-2/50	20 %
Bending modulus		ISO 178	3200 Mpa
bending strength		ISO 178	96.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.80MPa	ISO 75-1	84 °C
Hot deformation temperature	Hot deformation temperature	0.45Mpa	ISO 75-2	94 °C
Vicat softening temperature		ISO 306	97 °C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	0.6
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	0.7
UL flame retardant rating		UL 94	V-0
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	94.0 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	84.0 °C
Vicat softening temperature		ISO 306/B50	97.0 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	7E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	Flow		0.4-0.6 %
	Shrinkage rate	Across Flow		0.4-0.6 %
		Shrinkage rate	TD:4.00mm	Internal Method	0.40-0.60 %
		Shrinkage rate	Shrinkage rate	MD:4.00mm	Internal Method	0.40-0.60 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1E+16 ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/ABS MULTILON® TN-7000F TEIJIN JAPAN

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet