HDPE

HDPE UNIVL™ DMDD-6200 DOW JAPAN

257

Unit Price:US$ 1,249 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ASTM D1822	210 kJ/m²

Basic Performance	Test Condition	Test Method	Test Result
density		ASTM D-792	0.953
melt mass-flow rate	190℃/2.16kg	ASTM D-1238	0.25 g/10min
melt mass-flow rate	melt mass-flow rate	190℃/21.6kg	ASTM D-1238	23 g/10min

mechanical properties	Test Condition	Test Method	Test Result
Environmental stress cracking resistance	50℃，10% Igepal，F50	ASTM D-1693	50 hr
tensile strength	Yield	ASTM D-638	26.2 Mpa
tensile strength	tensile strength	Break	ASTM D-638	25.5 Mpa
elongation at yield		ASTM D-638	6 %
Elongation at Break		ASTM D-638	900 %
Bending modulus	2% Secant	ASTM D-790B	1020 Mpa
Impact strength of cantilever beam gap		ASTM D-1822	210 KJ/m
Shore hardness	Shore D	ASTM D-2240	59
tensile strength	Yield	ASTM D638	26.2 Mpa
tensile strength	tensile strength	Break	ASTM D638	25.5 Mpa
elongation	Yield	ASTM D638	6.0 %
elongation	elongation	Break	ASTM D638	900 %
Bending modulus	2%Secant	ASTM D790B	1020 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa，Unannealed	ASTM D-648	70 °C
Vicat softening temperature		ASTM D-1525	129 °C
Melting temperature		Internal Method	132 °C
Crystallization peak temperature		Internal Method	119 °C
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	70.0 °C
Brittle temperature		ASTM D746	<-76.1 °C
Vicat softening temperature		ASTM D1525	129 °C
Melting temperature		Internal Method	132 °C
Crystallization peak temperature	DSC	Internal Method	119 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	190°C/2.16kg	ASTM D1238	0.25 g/10min
melt mass-flow rate	melt mass-flow rate	190°C/21.6kg	ASTM D1238	23 g/10min
Environmental stress cracking resistance	50°C,100%Igepal,F50	ASTM D1693	50.0 hr

hardness	Test Condition	Test Method	Test Result
Shore hardness	ShoreD	ASTM D2240	59

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

HDPE UNIVL™ DMDD-6200 DOW JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet