PBT

PBT Toraycon® 5101G-15 TORAY JAPAN

277

Unit Price:US$ 2,966 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
40.2MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance｜Fast forming cycle
Application Areas:Automotive Applications｜Electrical components
Color:--
Grade:Enhanced level

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			15%玻璃纤维增强级.高抗冲击级

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	60 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ISO 527-2	5000 Mpa
tensile strength	Yield,23°C	ISO 527-2	90.0 Mpa
Tensile strain	Break,23°C	ISO 527-2	4.0 %
Bending modulus	23°C	ISO 178	4700 Mpa
bending strength	23°C	ISO 178	145 Mpa
Friction coefficient			0.19
Friction coefficient vs. Metal		SuzukiMethod	0.14
tensile strength	23℃	ASTM D638	95 Mpa
elongation	23℃	ASTM D638	5 %
bending strength	23℃	ASTM D790	125 Mpa
Bending modulus	23℃	ASTM D790	4.7 GPa
Impact strength of cantilever beam gap	Notched，23℃	ASTM D256	130 J/m
	Impact strength of cantilever beam gap	Notched，-40℃	ASTM D256	100 J/m
		Impact strength of cantilever beam gap	Unnotched，-40℃	ASTM D256	40 KJ/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Unnotched，23℃	ASTM D256	60 KJ/m
Rockwell hardness		ASTM D785	89 M
Friction coefficient	对金属	ASTM D1894	0.14
Friction coefficient	Friction coefficient	对本身	ASTM D1894	0.19
Impact strength of cantilever beam gap		ASTM D256/ISO 179	130 kg·cm/cm(J/M)ft·lb/in
	Impact strength of cantilever beam gap		ASTM D256/ISO 179	100 kg·cm/cm(J/M)ft·lb/in
		Impact strength of cantilever beam gap		ASTM D256/ISO 179	60 kg·cm/cm(J/M)ft·lb/in
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	40 kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	5 %
tensile strength		ASTM D638/ISO 527	95 kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	M89
Bending modulus		ASTM D790/ISO 178	4700 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	125 kg/cm²(MPa)[Lb/in²]

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD：-30to100°C	ISO 11359-2	5.5E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	220 °C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	195 °C
		Hot deformation temperature	0.45MPa	ASTM D648	220 °C
		Hot deformation temperature	Hot deformation temperature	1.82Mpa	ASTM D648	204 °C
Linear coefficient of thermal expansion		ASTM D696	5.5
UL flame retardant rating		UL 94	HB
Combustibility (rate)		UL 94	HB
Hot deformation temperature	HDT	ASTM D648/ISO 75	204 ℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	5.5x10^-5 mm/mm.℃

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD:3.00mm2	Internal Method	1.5 %
Shrinkage rate	Shrinkage rate	MD:3.00mm4	Internal Method	0.60 %
Water absorption rate	23°C,24hr	ISO 62	0.070 %
Water absorption rate	Water absorption rate	23℃,24hr	ASTM D570	0.07 %
density		ASTM D792/ISO 1183	1.36
Water absorption rate		ASTM D570/ISO 62	0.07 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	4E+16 ohms·cm
Dielectric strength		IEC 60243-1	22 KV/mm
Dielectric constant	23°C,50Hz	IEC 60250	3.40
Dielectric constant	Dielectric constant	23°C,1kHz	IEC 60250	3.50
Dissipation factor	23°C,50Hz	IEC 60250	1E-03
Dissipation factor	Dissipation factor	23°C,1MHz	IEC 60250	0.020
Arc resistance		IEC 60950	110 sec
Compared to the anti leakage trace index	CTI	UL 746	PLC 0
Volume resistivity		ASTM 257	2.0
Dielectric strength		ASTM D149	22 MV/m
Dielectric constant	50Hz	ASTM D150	3.4
Dielectric constant	Dielectric constant	10	ASTM D150	3.5
Dielectric loss	50Hz，Tangent	ASTM D150	0.001
Dielectric loss	Dielectric loss	10，Tangent	ASTM D150	0.02
Arc resistance		ASTM D495	110 S
Dielectric constant		ASTM D150/IEC 60250	3.4
Volume resistivity		ASTM D257/IEC 60093	2.0X10^14 Ω.cm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Sale,23°C	ISO 2039-2	64

Supplementary Information	Test Condition	Test Method	Test Result
BarFlowLength	250°C,1.00mm	Internal Method	8.50 CM

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.