PC LNP™ THERMOCOMP™ DX11355-BKNAT SABIC INNOVATIVE NANSHA

274

Unit Price:US$ 8,964 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
88MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜High mobility
Application Areas:Automotive components｜Electronic and electrical components
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ASTM D4812	2100 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.60mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	2600 Mpa
tensile strength	Yield		58 Mpa
tensile strength	tensile strength	Break		52 Mpa
elongation	Yield		5.4 %
elongation	elongation	Break		70 %
Bending modulus	50.0 mm Span	ASTM D790	2400 Mpa
bending strength	Yield, 50.0 mm Span		90 Mpa
bending strength	bending strength	Break, 50.0 mm Span		89 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			100 to 110 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.02 %
Suggested injection volume			30 to 80 %
Hopper temperature			60 to 80 °C
Temperature at the rear of the barrel			250 to 290 °C
Temperature in the middle of the barrel			255 to 295 °C
Temperature at the front of the material cylinder			260 to 300 °C
Spray nozzle temperature			275 to 300 °C
Processing (melt) temperature			275 to 300 °C
Mold temperature			60 to 90 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.038 to 0.076 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	114 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C		0.000062 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	垂直 : -40 to 40°C		0.000067 cm/cm/°C
RTI Elec		UL 746B	80 °C
RTI Imp		UL 746B	80 °C
RTI		UL 746B	80 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	12 g/10 min
Shrinkage rate	Flow : 24hr		0.5 %
Shrinkage rate	Shrinkage rate	Across FlowFlow : 24hr		0.5 %
Water absorption rate	24 hr, 23°C, 50% RH	ASTM D570	0.01 %

Electrical performance	Test Condition	Test Method	Test Result
Relative permittivity	1.00 GHz	IEC 60250	2.92
Dissipation factor	1.00 GHz	IEC 60250	0.007

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LNP™ THERMOCOMP™ DX11355-BKNAT SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet Compare

Technical Data Sheet