PA66

PA66 Ultramid® A3W BASF MALAYSIA

194

Unit Price:US$ 4,791 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
PA66 Ultramid® A3W BASF GERMANY

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Oil resistant｜Fast forming cycle｜High mobility｜heat-resisting
Application Areas:wheel｜Engine parts｜Laptop case｜bearing
Color:--
Grade:Enhanced level

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂

flammability	Test Condition	Test Method	Test Result
Flammability level		UL 94	V-2
Polymer Abbreviation			PA66

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	3000 Mpa
tensile strength	Yield	ISO 527-2/50	85.0 Mpa
Tensile strain	Yield	ISO 527-2/50	4.4 %
Nominal tensile fracture strain		ISO 527-2/50	25 %
Tensile creep modulus	1000 hr	ISO 899-1	-- Mpa
Bending modulus		ISO 178	2900 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
drying time			4.0 hr
Suggested maximum moisture content			0.15 %
Hopper temperature			80 °C
Temperature at the rear of the barrel			290 °C
Temperature in the middle of the barrel			290 °C
Temperature at the front of the material cylinder			290 °C
Spray nozzle temperature			290 °C
Processing (melt) temperature			280 to 300 °C
Mold temperature			60 to 80 °C
Residence Time			< 10.0 min
Screw speed			< 18 m/min

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	220 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	75.0 °C
Melting temperature		ISO 11357-3	260 °C
Linear coefficient of thermal expansion	23 to 80°C，Flow	ISO 11359-2	7.0E-5 - 1.0E-4 cm/cm/°C
specific heat			1700 J/kg/°C
thermal conductivity		DIN 52612	0.33 W/m/K
Temperature index - at 50% loss of tensile strength	--5	IEC 60216	147 °C
Temperature index - at 50% loss of tensile strength	Temperature index - at 50% loss of tensile strength	--6	IEC 60216	121 °C
Maximum operating temperature	短周期操作		200 °C

Physical properties	Test Condition	Test Method	Test Result
Apparent density			0.70 g/cm³
Melt Volume Flow Rate (MVR)	275°C/5.0 kg	ISO 1133	100 cm3/10min
Shrinkage rate	横向Flow	ISO 294-4	1.7 %
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	1.4 %
Water absorption rate	Saturation, 23°C	ISO 62	8.0 to 9.0 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	2.5 to 3.1 %
Stickiness	96% H2SO4	ISO 307	150 cm³/g
Mold Shrinkage - Constrained			0.85 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	-- ohms
Volume resistivity		IEC 60093	1.0E+15 ohms·cm
Relative permittivity	1 MHz	IEC 60250	3.20
Dissipation factor	1 MHz	IEC 60250	0.025
Compared to the anti leakage trace index	Solution A	IEC 60112	PLC 1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.