PPS

PPS DURAFIDE® 6465A6 JAPAN POLYPLASTIC

212

Unit Price:US$ 4,984 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
47.4MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜High gloss｜Flame retardant｜Glass fiber reinforced｜enhance
Application Areas:Household appliances｜Fiber grade
Color:--
Grade:Enhanced level

Material Certification

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-0

Basic Performance	Test Condition	Test Method	Test Result
Melt viscosity		ISO 11443	280 Pa.s
Melt viscosity	Melt viscosity		ASTM D3835	270 Pa.s

mechanical properties	Test Condition	Test Method	Test Result
Tensile stress	Yield	ISO 527-2	140 MPa
Tensile stress	Tensile stress	Yield	ASTM D638	145 MPa
elongation	Break	ASTM D638	1.2 %
elongation	elongation	Break	ISO 527-2	1.0 %
Charpy Notched Impact Strength		ISO 179/1eA	6.0 kJ/m²
Impact strength of cantilever beam gap		ASTM D256	75 J/m
tensile strength		ISO 527-2	140 Mpa
Tensile strain	Break	ISO 527-2	1.0 %
Bending modulus		ISO 178	19000 Mpa
bending strength		ISO 178	200 Mpa
tensile strength		ASTM D638/ISO 527	140 kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	19000 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	200 kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	1 %

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	275 ℃
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2A	270 ℃
UL flame retardant rating		UL 94	V-0
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	270 °C
Linear coefficient of thermal expansion	MD	Internal Method	1E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	Internal Method	3E-05 cm/cm/°C
Combustibility (rate)		UL 94	V-0
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	- mm/mm.℃

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	23°C,24hr	ISO 62	0.030 %
Melt viscosity	310°C,1000sec^-1	ISO 11443	280000 mPa·s
density		ASTM D792/ISO 1183	1.95
Water absorption rate		ASTM D570/ISO 62	- %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	2E+15 ohms·cm
Dielectric strength	3.00mm	IEC 60243-1	15 KV/mm
Relative permittivity	1kHz	IEC 60250	4.80
Relative permittivity	Relative permittivity	1MHz	IEC 60250	4.80
Dissipation factor	1kHz	IEC 60250	2E-03
	Dissipation factor	1MHz	IEC 60250	2E-03
	Dissipation factor	Dissipation factor	耐电弧性	IEC 60250	170 sec
Compared to the anti leakage trace index		IEC 60112	PLC 3
Volume resistivity		ASTM D257/IEC 60093	- Ω.cm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Scale	ISO 2039-2	105

Supplementary Information	Test Condition	Test Method	Test Result
ColourNumber			HD9050

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.