Material Description

Material Properties:High mobility｜Ductility at low temperature｜Short molding cycle
Application Areas:Electronic and Electrical Applications｜Aerospace Applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	25 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	60 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	-30°C	ASTM D256	560 J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	730 J/m
		Impact strength of cantilever beam gap	-30°C	ISO 180/1A	20 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	55 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	NoBreak
Dart impact	23°C,TotalEnergy	ASTM D3763	67.9 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	5VA
Burning wire flammability index	1.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	825 °C
Extreme Oxygen Index		ISO 4589-2	40 %

mechanical properties	Test Condition	Test Method	Test Result
elongation	Yield	ASTM D638	5.8 %
Tensile strain	Yield	ISO 527-2/50	5.0 %
elongation	Break	ASTM D638	100 %
Tensile strain	Break	ISO 527-2/50	100 %
Bending modulus	50.0mmSpan	ASTM D790	2340 Mpa
Bending modulus	Bending modulus		ISO 178	2300 Mpa
bending strength		ISO 178	88.0 Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	95.1 Mpa
Tensile modulus		ASTM D638	2270 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	2200 Mpa
tensile strength	Yield	ASTM D638	58.1 Mpa
	tensile strength	Yield	ISO 527-2/50	59.0 Mpa
		tensile strength	Break	ASTM D638	58.5 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	55.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	7.2E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to80°C	ISO 11359-2	7.5E-05 cm/cm/°C
RTI Elec		UL 746	130 °C
RTI Imp		UL 746	50.0 °C
RTI Str		UL 746	50.0 °C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	136 °C
	Hot deformation temperature	0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	136 °C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	124 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	124 °C
Vicat softening temperature		ASTM D152510	143 °C
	Vicat softening temperature	--	ISO 306/B50	143 °C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	144 °C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	7.2E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to80°C	ISO 11359-2	7.5E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792	1.18 g/cm³
density	density		ISO 1183	1.19 g/cm³
melt mass-flow rate	300°C/1.2kg	ASTM D1238	17 g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	16.0 cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.40-0.80 %
Shrinkage rate	Shrinkage rate	TD：3.20mm	Internal Method	0.40-0.80 %
Water absorption rate	Saturation,23°C	ISO 62	0.35 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15 %

Electrical performance	Test Condition	Test Method	Test Result
Dielectric strength	3.20mm,in Oil	IEC 60243-1	19 KV/mm
Relative permittivity	50Hz	IEC 60250	2.70
	Relative permittivity	60Hz	IEC 60250	2.70
	Relative permittivity	Relative permittivity	1MHz	IEC 60250	2.70
Dissipation factor	50Hz	IEC 60250	4E-04
	Dissipation factor	60Hz	IEC 60250	4E-04
	Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.010
Compared to the anti leakage trace index		IEC 60112	PLC 3

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test	H358/30	ISO 2039-1	95.0 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.