Material Properties:Chemical resistance｜Flame retardant｜Glass fiber reinforced｜High impact resistance｜High temperature resistance
Application Areas:Automotive sector｜Electrical components｜sporting goods｜small home appliances
Color:--
Grade:Injection grade
Material Certification
UL
Technical Data Sheet
other
Test Condition
Test Method
Test Result
characteristic
40%加纤.增强.标准
Other performance
Test Condition
Test Method
Test Result
320℃,98MPa，Flow长
TORAY
100
impact performance
Test Condition
Test Method
Test Result
Impact strength of simply supported beam without notch
23°C
ISO 179
55 kJ/m²
flammability
Test Condition
Test Method
Test Result
UL flame retardant rating
0.28mm
UL 94
V-0
Basic Performance
Test Condition
Test Method
Test Result
Water absorption rate
24hr,23℃于水中
ASTM D-570
0.02 %
mechanical properties
Test Condition
Test Method
Test Result
Charpy Notched Impact Strength
ASTM D256/ISO 179
11 kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength
ASTM D256/ISO 179
55 kg·cm/cm(J/M)ft·lb/in
Elongation at Break
ASTM D638/ISO 527
1.8 %
tensile strength
ASTM D638/ISO 527
200 kg/cm²(MPa)[Lb/in²]
Rockwell hardness
ASTM D785
122
Bending modulus
ASTM D790/ISO 178
15.5 kg/cm²(MPa)[Lb/in²]
bending strength
ASTM D790/ISO 178
305 kg/cm²(MPa)[Lb/in²]
Elongation at Break
23℃
ASTM D-638
3.6 %
Impact strength of cantilever beam gap
Notched
ASTM D-256
130 J/m
Impact strength of cantilever beam gap
Unnotched
ASTM D-256
55 KJ/m
Bending modulus
23℃
ASTM D-790
13.3 GPa
tensile strength
23℃
ASTM D-638
207 Mpa
bending strength
23℃
ASTM D-790
275 Mpa
Rockwell hardness
ASTM D-785
122 R
compressive strength
ASTM D-732
80
Taber abraser
1000Cycles
ISO 9352
50.0 mg
tensile strength
Yield,23°C
ISO 527-2
200 Mpa
Tensile strain
Break,23°C
ISO 527-2
1.8 %
Bending modulus
23°C
ISO 178
15500 Mpa
bending strength
23°C
ISO 178
305 Mpa
shear strength
23°C
JISK7214
80.0 Mpa
Friction coefficient
0.25
thermal performance
Test Condition
Test Method
Test Result
Combustibility (rate)
UL 94
V-0
Hot deformation temperature
HDT
ASTM D648/ISO 75
>260 ℃（℉）
Melting temperature
278 ℃（℉）
Hot deformation temperature
1.82MPa
ASTM D-648
>260 °C
Linear coefficient of thermal expansion
Flow
ASTM D-696
2.3
Linear coefficient of thermal expansion
Across Flow
ASTM D-696
3.2
Melting temperature
DSC
278 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
260 °C
Melting temperature
ISO 11357-3
278 °C
Linear coefficient of thermal expansion
MD
ISO 11359-2
2.3E-05 cm/cm/°C
Linear coefficient of thermal expansion
TD
ISO 11359-2
3.1E-05 cm/cm/°C
Physical properties
Test Condition
Test Method
Test Result
density
ASTM D792/ISO 1183
1.66
Shrinkage rate
ASTM D955
0.36 %
Water absorption rate
ASTM D570/ISO 62
0.02 %
Shrinkage rate
Across Flow
TORAY
0.70 %
Taber wear resistance
ASTM D-D1044
50 mg/1000次
Friction coefficient
对铁
ASTM D-1894
0.25
limiting pv value
TORAY
815 KJ/m
Shrinkage rate
Flow
TORAY
0.20 %
Shrinkage rate
TD:3.00mm2
Internal Method
0.80 %
Shrinkage rate
MD:3.00mm4
Internal Method
0.20 %
Water absorption rate
23°C,24hr
ISO 62
0.020 %
Electrical performance
Test Condition
Test Method
Test Result
Dielectric constant
ASTM D150/IEC 60250
4.2
Volume resistivity
ASTM D257/IEC 60093
1014 Ω.cm
Dielectric constant
10
ASTM D-150
3.8
Volume resistivity
ASTM D-257
10 Ω.m
Arc resistance
ASTM D-495
127
Dissipation factor
10
ASTM D-150
0.002
Dielectric strength
ASTM D-149
21 MV/m
Volume resistivity
IEC 60093
1E+16 ohms·cm
Dielectric strength
IEC 60243-1
24 KV/mm
Dielectric constant
23°C,1MHz
IEC 60250
4.20
Dissipation factor
23°C,1MHz
IEC 60250
2E-03
hardness
Test Condition
Test Method
Test Result
Rockwell hardness
R-Scale
ISO 2039-2
122
Supplementary Information
Test Condition
Test Method
Test Result
BarFlowLength
320°C,1.00mm
Internal Method
135 mm
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)