PC/ABS

PC/ABS CYCOLOY™ CX7110 SABIC INNOVATIVE NANSHA

219

Unit Price:US$ 3,535 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜High mobility
Application Areas:Automotive sector｜Electronic field｜Electrical field
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	15 kJ/m²
Dart impact	23°C, Total Energy	ASTM D3763	63.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75 mm	UL 94	V-2
	UL flame retardant rating	1.0 mm	UL 94	V-1
		UL flame retardant rating	1.2 mm	UL 94	V-0
		UL flame retardant rating	UL flame retardant rating	1.8 mm	UL 94	5VB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--2	ASTM D638	2900 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2700 Mpa
tensile strength	Yield3	ASTM D638	64.0 Mpa
	tensile strength	Yield	ISO 527-2/50	61.0 Mpa
		tensile strength	Break3	ASTM D638	54.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	51.0 Mpa
elongation	Yield3	ASTM D638	4.0 %
	elongation	Yield	ISO 527-2/50	4.0 %
		elongation	Break3	ASTM D638	90 %
		elongation	elongation	Break	ISO 527-2/50	90 %
Bending modulus	50.0 mm Span4	ASTM D790	2700 Mpa
Bending modulus	Bending modulus	--5	ISO 178	2500 Mpa
bending strength	--5,6	ISO 178	100 Mpa
bending strength	bending strength	Yield, 50.0 mm Span4	ASTM D790	100 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			80 to 90 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.040 %
Suggested injection volume			30 to 80 %
Temperature at the rear of the barrel			220 to 255 °C
Temperature in the middle of the barrel			220 to 265 °C
Temperature at the front of the material cylinder			245 to 275 °C
Spray nozzle temperature			245 to 275 °C
Processing (melt) temperature			245 to 275 °C
Mold temperature			60 to 80 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.038 to 0.076 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	94.0 °C
	Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	98.0 °C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	84.0 °C
			Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	90.0 °C
			Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	84.0 °C
Vicat softening temperature	--	ASTM D152510	102 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	103 °C
Ball Pressure Test	73 to 77°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.5E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.5E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	7.5E-5 cm/cm/°C
thermal conductivity		ISO 8302	0.20 W/m/K

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	260°C/2.16 kg	ASTM D1238	22 g/10 min
Melt Volume Flow Rate (MVR)	260°C/2.16 kg	ISO 1133	21.0 cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.40 - 0.60 %
Water absorption rate	Saturation, 23°C	ISO 62	0.20 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.10 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.