PBT

PBT CELANEX® 3309HR CELANESE USA

218

Unit Price:US$ 4,759 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Hydrolysis resistance｜Filler: Glass fiber reinforced material｜30% filler by weight
Application Areas:Automotive sector｜Electronic and electrical accessories
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	8.5 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	8.5 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	45 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	46 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	12 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	35 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.70mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1A/1	9200 Mpa
tensile strength	Break,23°C	ASTM D638	137 Mpa
tensile strength	tensile strength	Break	ISO 527-2/1A/5	139 Mpa
elongation	Break,23°C	ASTM D638	2.8 %
Tensile strain	Break	ISO 527-2/1A/5	2.7 %
Bending modulus	23°C	ISO 178	8700 Mpa
bending strength	23°C	ISO 178	210 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	225 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	205 °C
Glass transition temperature		ISO 11357-2	60.0 °C
Vicat softening temperature		ISO 306/B50	220 °C
Melting temperature		ISO 11357-3	225 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	2.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	1E-04 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD	ISO 294-4	0.70-0.90 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.30-0.50 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.16 %
density		ASTM D792	1.53 g/cm³
density	density		ISO 1183	1.54 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index		IEC 60112	PLC 1
Surface resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Dielectric strength		IEC 60243-1	31 KV/mm
Relative permittivity	100Hz	IEC 60250	4.50
Relative permittivity	Relative permittivity	1MHz	IEC 60250	4.10
Dissipation factor	100Hz	IEC 60250	2.2E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.016

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT CELANEX® 3309HR CELANESE USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet