POM Delrin® 500AL NC010 DUPONT JAPAN

378

Unit Price:US$ 5,976 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Dimensional stability｜Fatigue resistance｜High impact resistance
Application Areas:Household appliances｜Bottle cap｜Industrial applications｜Automotive sector｜Electronic field｜Electrical field｜Non specific food applications
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	130 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	160 kJ/m²

flammability	Test Condition	Test Method	Test Result
FMVSS flammability		FMVSS302	B
Burning rate	1.00mm	ISO 3795	28 mm/min
UL flame retardant rating	0.75mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
		UL flame retardant rating	0.75mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	3000 Mpa
tensile strength	Yield	ISO 527-2	66.0 Mpa
Tensile strain	Yield	ISO 527-2	11 %
Nominal tensile fracture strain		ISO 527-2	23 %
Tensile creep modulus	1hr	ISO 899-1	2400 Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	1600 Mpa
Bending modulus		ISO 178	2800 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	164 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	97.0 °C
Melting temperature		ISO 11357-3	178 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.2E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	1.2E-04 cm/cm/°C
AnnealingTemperature			160 °C
AnnealingTime-Optional			30.0 min/mm

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate		ISO 1133	14 g/10min
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	12.0 cm3/10min
Shrinkage rate	TD	ISO 294-4	1.7 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	1.8 %
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.30 %

Supplementary Information	Test Condition	Test Method	Test Result
Emission		VDA275	<8.00 mg/kg

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

POM Delrin® 500AL NC010 DUPONT JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet