PC LNP™ THERMOCOMP™ DX15354 BKNAT SABIC INNOVATIVE NANSHA

227

Unit Price:US$ 9,719 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
19.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant
Application Areas:Electronic appliances
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ASTM D4812	2200 J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C4	ISO 180/1U	180 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
elongation	Break	ISO 527-2/50	11 %
Bending modulus	--	ASTM D790	2890 Mpa
Bending modulus	Bending modulus	--	ISO 178	2880 Mpa
bending strength	--	ASTM D790	111 Mpa
bending strength	bending strength	--	ISO 178	112 Mpa
Tensile modulus	--2	ASTM D638	2920 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2940 Mpa
tensile strength	Break3	ASTM D638	59.0 Mpa
tensile strength	tensile strength	Break	ISO 527-2/50	58.0 Mpa
elongation	Break3	ASTM D638	11 %

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	168 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	155 °C
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	6.3E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	6.7E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	330°C/2.16kg	ISO 1133	63.0 cm3/10min
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.13 %

Electrical performance	Test Condition	Test Method	Test Result
Dielectric constant	1.10GHz	Internal Method	2.95
Dissipation factor	1.10GHz	Internal Method	6E-03

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LNP™ THERMOCOMP™ DX15354 BKNAT SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet Compare

Technical Data Sheet