PC LEXAN™ BX7241-BR6G159 SABIC INNOVATIVE NANSHA

185

Unit Price:US$ 3,297 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Low temperature resistance｜Flame retardant
Application Areas:Plastic bag｜Lighting applications｜Thin walled components
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
-30°C		ASTM D256	190 J/m
0°C		ASTM D256	420 J/m
23°C		ASTM D256	690 J/m
-30°C		ISO 180/1A	11 kJ/m²
0°C		ISO 180/1A	11 kJ/m²
23°C		ISO 180/1A	28 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	60.0 J

flammability	Test Condition	Test Method	Test Result
Burning wire flammability index	0.750mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.00mm	IEC 60695-2-13	800 °C
	Hot filament ignition temperature	1.50mm	IEC 60695-2-13	825 °C
	Hot filament ignition temperature	Hot filament ignition temperature	3.00mm	IEC 60695-2-13	825 °C
UL flame retardant rating	0.200mm	UL 94	V-2
	UL flame retardant rating	0.500mm	UL 94	V-1
		UL flame retardant rating	0.600mm	UL 94	V-0
			UL flame retardant rating	1.50mm	UL 94	5VB
			UL flame retardant rating	UL flame retardant rating	3.00mm	UL 94	5VA

mechanical properties	Test Condition	Test Method	Test Result
--1		ASTM D638	2500 Mpa
yield		ASTM D638	67.0 Mpa
yield	yield		ISO 527-2/50	62.0 Mpa
crack		ASTM D638	65.0 Mpa
crack	crack		ISO 527-2/50	45.0 Mpa
yield		ASTM D638	4.4 %
yield	yield		ISO 527-2/50	4.2 %
crack		ASTM D638	120 %
crack	crack		ISO 527-2/50	90 %
50.0mm span		ASTM D790	2450 Mpa
--7		ISO 178	2600 Mpa
--8		ISO 178	98.0 Mpa
--9		ISO 178	99.0 Mpa
Yield, 50.0mm span		ASTM D790	107 Mpa
Fracture, 50.0mm span		ASTM D790	105 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	103 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	93.0 °C
Ball Pressure Test	75°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	5.9E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	5.9E-05 cm/cm/°C
RTI Elec		UL 746	80.0 °C
RTI Imp		UL 746	80.0 °C
RTI		UL 746	80.0 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	260°C/2.16kg	ASTM D1238	18 g/10min
Melt Volume Flow Rate (MVR)	260°C/2.16kg	ISO 1133	18.0 cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.40-0.60 %
Water absorption rate	Saturation,23°C	ISO 62	0.20 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.10 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		ASTM D257	>2.0E+15 ohms
Volume resistivity		ASTM D257	>1.0E+16 ohms·cm
Compared to the anti leakage trace index	CTI	UL 746	PLC 3
Hot wire ignition	HWI	UL 746	PLC 4

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LEXAN™ BX7241-BR6G159 SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet Compare

Technical Data Sheet