POM

POM LNP™ LUBRICOMP™ KL-4540D SABIC INNOVATIVE US

233

Unit Price:US$ 3,383 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Low extract｜Internal lubrication
Application Areas:Medical and nursing supplies｜Electrical appliances｜Plastic bag
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	--	ISO 6603-2	1.00 J
Dart impact	Dart impact	23°C, Energy at Peak	ASTM D3763	3.00 J
Suspended wall beam without notch impact strength	23°C6	ISO 180/1U	42 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ASTM D4812	620 J/m

mechanical properties	Test Condition	Test Method	Test Result
Wear factor		ASTM D3702	1.8E+6 10^-8 mm³/N·m
Friction coefficient	Static	ASTM D3702	0.14
Friction coefficient	Friction coefficient	Dynamic	ASTM D3702	0.25
bending strength	Break, 50.0 mm Span3	ASTM D790	63.0 Mpa
bending strength	bending strength	--	ISO 178	60.0 Mpa
Bending modulus	--4	ISO 178	2080 Mpa
Bending modulus	Bending modulus	50.0 mm Span3	ASTM D790	2020 Mpa
elongation	Break	ISO 527-2/5	43 %
	elongation	Break2	ASTM D638	30 %
		elongation	Yield	ISO 527-2/5	22 %
		elongation	elongation	Yield2	ASTM D638	14 %
tensile strength	Break	ISO 527-2/5	39.0 Mpa
	tensile strength	Break2	ASTM D638	43.0 Mpa
		tensile strength	Yield	ISO 527-2/5	39.0 Mpa
		tensile strength	tensile strength	Yield2	ASTM D638	43.0 Mpa
Tensile modulus	--	ISO 527-2/1	2020 Mpa
Tensile modulus	Tensile modulus	--1	ASTM D638	1830 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
drying time			4.0 hr
Temperature at the rear of the barrel			175 to 190 °C
Temperature in the middle of the barrel			195 to 205 °C
Temperature at the front of the material cylinder			210 to 220 °C
Processing (melt) temperature			200 to 215 °C
Mold temperature			80 to 110 °C
Back pressure			0.200 to 0.300 Mpa
Screw speed			30 to 60 rpm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	87.0 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span6	ISO 75-2/Af	79.0 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	1.1E-4 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	1.1E-4 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.43 %
Water absorption rate	Water absorption rate	24 hr, 50% RH	ASTM D570	0.18 %
Shrinkage rate	Across FlowFlow : 24hr	ASTM D955	2.1 - 2.9 %
Shrinkage rate	Shrinkage rate	Flow : 24hr	ASTM D955	2.1 - 2.9 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

POM LNP™ LUBRICOMP™ KL-4540D SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet