PC LEXAN™  LUX9612G-WH8A508X SABIC INNOVATIVE NANSHA

195
  • Unit Price:US$ 4,599 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    23.8MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Flame retardant
  • Application Areas:Plastic bag｜Lighting applications
  • Color:--
  • Grade:Flame retardant grade

Technical Data Sheet

optical performanceTest ConditionTest MethodTest Result
Refractive indexISO 4891.586
impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength23°CASTMD4812无断裂
Suspended wall beam without notch impact strength-30°C5ISO 180/1U无断裂
Multi axis Instrumented Impact EnergyISO 6603-2130 J
Impact strength of cantilever beam gap23°CISO 180/1A40 kJ/m²
Dart impact23°C,TotalEnergyASTM D376370.0 J
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.30mmUL 94V-2
UL flame retardant rating1.5mmUL 94V-0
Burning wire flammability index0.8mmIEC 60695-2-12750 °C
Burning wire flammability index1.0mmIEC 60695-2-12960 °C
Burning wire flammability index1.5mmIEC 60695-2-12850 °C
Hot filament ignition temperature1.0mmIEC 60695-2-13850 °C
Hot filament ignition temperature1.5mmIEC 60695-2-13850 °C
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusISO 527-2/12300 Mpa
tensile strengthYieldISO 527-2/5063.0 Mpa
tensile strengthBreakISO 527-2/5065.0 Mpa
Tensile strainYieldISO 527-2/506.0 %
Tensile strainBreakISO 527-2/50100 %
Bending modulusISO 1782250 Mpa
bending strengthISO 17894.0 Mpa
Tensile modulusASTM D6382300 Mpa
Tensile modulusISO 527-2/12230 Mpa
tensile strengthYieldASTM D63862.0 Mpa
tensile strengthYieldISO 527-2/5062.0 Mpa
tensile strengthBreakASTM D63865.0 Mpa
tensile strengthBreakISO 527-2/5058.0 Mpa
elongationYieldASTM D6386.0 %
elongationBreakASTM D63880 %
Tensile strainBreakISO 527-2/5075 %
Bending modulus50.0mmSpanASTM D7902160 Mpa
Bending modulusISO 1782250 Mpa
bending strengthISO 17895.0 Mpa
bending strengthYield,50.0mmSpanASTM D79095.0 Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45MPa,Unannealed,64.0mmSpanISO 75-2/Bf135 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af123 °C
Vicat softening temperature--ISO 306/B50141 °C
Vicat softening temperature--ISO 306/B120142 °C
Ball Pressure Test125°CIEC 60695-10-2通过
Linear coefficient of thermal expansionMD:-40to40°CASTME8316.8E-05 cm/cm/°C
Linear coefficient of thermal expansionTD:-40to40°CASTME8316.7E-05 cm/cm/°C
specific heatASTMC3511260 J/kg/°C
thermal conductivityASTMC1770.20 W/m/K
RTI ElecUL 746125 °C
RTI ImpUL 746115 °C
RTIUL 746125 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648123 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af123 °C
Vicat softening temperatureASTM D152510140 °C
Ball Pressure Test125°CIEC 60695-10-2Pass
RTI StrUL 746125 °C
Hot deformation temperature0.45MPa,Unannealed,64.0mmSpanISO 75-2/Bf135 °C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rateSaturation,23°CISO 620.35 %
Water absorption rateEquilibrium,100°CASTM D5700.58 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.15 %
Outdoor applicabilityUL 746Cf2
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11337.00 cm3/10min
Shrinkage rateMD：3.20mmInternal Method0.50-0.70 %
melt mass-flow rate300°C/1.2kgASTM D12387.0 g/10min
Shrinkage rateMD：3.20mmInternal Method0.60-0.80 %
Electrical performanceTest ConditionTest MethodTest Result
Hot wire ignitionHWIUL 746PLC 3
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Dielectric strength3.20mm,inAirASTM D14915 KV/mm
Dielectric constant50HzASTM D1503.17
Dielectric constant60HzASTM D1503.17
Dielectric constant1MHzASTM D1502.96
Dissipation factor50HzASTM D1509E-04
Dissipation factor60HzASTM D1509E-04
Dissipation factor1MHzASTM D1500.010
Compared to the anti leakage trace indexCTIUL 746PLC 3
High arc combustion indexHAIUL 746PLC 1
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-ScaleASTM D785118
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.